Loading patent…
AssigneeChemische Werke Huls Aktiengesellschaft
InventorsFerdinand List, Otto Rauhut, Peter Hegenberg, Rudolf Strobele
Estimating the term…
Crude 1,10-decanedicarboxylic acid produced by the nitric acid oxidation at 20.degree.14 60.degree. C. of cyclododecanone, cyclododecanol or a mixture thereof can be purified by distillation to a purity suitable for use in the production of polyamides and polyesters by reducing prior to distillation, e.g., by heating to 70.degree.-90.degree. C., the organically bound nitrogen content and as required the nitric acid content, e.g., by washing, and water content thereof so that the sample which is distilled has maximum contents thereof of 0.05%, 0.02% and 0.1% by weight, respectively, and distilling the pre-purified sample at a sump temperature of 215.degree.-225.degree. C. and at a pressure of 0.5 - 2 torr.
A process for the production of 1,10-decanedicarboxylic acid with low melt color values from crude crystalline acid having an organically bound nitrogen content of 0.05% by weight or less and having a nitric acid content above 0.1% by weight and produced by oxidizing cyclododecanol, cyclododecanone or both with nitric acid at low temperature and under mild conditions and subjecting the thus-produced crude acid to a thermal treatment under oxidative conditions, at a temperature above the oxidation temperature, which reduces the organically bound nitrogen content of the crude acid to 0.05% by weight or less, which consists essentially of (a) reducing the nitric acid content of the starting crystalline crude acid to 0.02% by weight or less by a thermal treatment of the crude acid under vacuum at a temperature at which nitrous gases evolve from the crude acid and above the oxidation and thermal treatment temperatures employed to produce the starting crude crystalline acid;
A process for the production of 1,10-decanedicarboxylic acid with low melt color values from crude crystalline acid having an organically bound nitrogen content of 0.05% by weight or less and having a nitric acid content above 0.1% by weight and produced by oxidizing cyclododecanol, cyclododecanone or both with nitric acid at low temperature and under mild conditions and subjecting the thus-obtained crude acid to a thermal treatment under oxidative conditions, at a temperature above the oxidation temperature, which reduces the organically bound nitrogen content of the crude acid to 0.05% by weight or less, which consists essentially of (a) reducing the nitric acid content of the starting crystalline crude acid to 0.02% by weight or less by washing the crude acid with water and drying the washed acid to a water content of 0.1% by weight or less;
A process for the production of 1,10-decanedicarboxylic acid with low melt color values from crude crystalline acid having an organically bound nitrogen content of 0.05% by weight or less and having a nitric acid content above 0.1% by weight and produced by oxidizing cyclododecanol, cyclododecanone or both with nitric acid at low temperature and under mild conditions and subjecting the thus-produced crude acid to a thermal treatment under oxidative conditions, at a temperature above the oxidation temperature, which reduces the organically bound nitrogen content of the crude acid to 0.05% by weight or less, which consists essentially of (a) reducing the nitric acid content of the starting crystalline crude acid to 0.2% by weight or less by washing the crude acid with water and subjecting the washed acid to a thermal treatment under vacuum at a temperature at which nitrous gases evolve from the crude acid and above the oxidation and thermal treatment temperatures employed to produce the starting crude crystalline acid;
Dependencies are inferred from the claim text.