Method of preparing homogeneous thermosetting powder paint compositions

A method of preparing a powder paint composition comprising:

• A. passing a liquid paint composition comprising a solution of
• 1. a copolymer formed from glycidyl acrylate or glycidyl methacrylate and an ethylenically unsaturated monomer in such proportions as to obtain a copolymer with a glass transition temperature in the range of 40.degree. C to 90.degree. C and a number average molecular weight in the range of from 2500 to 8500;
• 2. a flow control agent;
• 3. pigment;
• and
• 4. inert solvent
• through an evaporating zone maintained under pressure said evaporating zone comprising a tortuous path of relatively narrow cross-section, elongated in a direction lateral to the direction of flow of said solution through said zone;
• B. heating said solution while it is confined within said evaporating zone to a temperature
• 1. above the melting point of said copolymer, but below the point at which degradation occurs;
• 2. above the temperature at which said inert solvent begins to vaporize
• thus inducing turbulent flow of said solution within said evaporating zone and thereby maintaining an intimate homogeneous mixture of the vapors of the volatile components of said solution and dispersed particles of nonvolatile components of said solution;
• C. passing said homogeneous mixture from said evaporating zone into a separating zone which is maintained under reduced pressure and, while maintaining the temperature within said separating zone above the melting point of said copolymer, causing said solvent vapor to be removed and allowing said nonvolatile components to collect in a molten state;
• D. removing said nonvolatile components from said separating zone;
• E. cooling said nonvolatile components to form a solid material;
• and
• F. pulverizing said solid material to form a uniformly pigmented powder.

A method of preparing a powder paint composition comprising:

• A. preparing a copolymer containing crosslinkable functional groups by solution polymerization in an inert solvent, said copolymer having a glass transition temperature of between 40.degree. C and 90.degree. C and a number average molecular weight of between about 1,000 and about 15,000;
• B. introducing a flow control agent;
• C. introducing pigment into said copolymer solution;
• D. passing a solution comprising the ingredients of (A), (B) and (C) into an evaporating zone comprising a tortuous path of relatively narrow cross-section, elongated in a direction lateral to the direction of flow of said solution through said zone;
• E. heating said solution while it is confined within said evaporating zone to a temperature
• 1. above the melting point of said copolymer, but below the point at which degradation occurs;
• 2. above the temperature at which said inert solvent begins to vaporize,
• thus inducing turbulent flow of said solution within said evaporating zone and thereby maintaining an intimate homogeneous mixture of the vapors of the volatile components of said solution and dispersed particles of nonvolatile components of said solution;
• F. passing said homogeneous mixture from said evaporating zone into a separating zone and, while maintaining the temperature within said separating zone above the melting point of said copolymer, causing said solvent vapor to be removed and allowing said nonvolatile components to collect in a molten state;
• G. removing said nonvolatile components from said separating zone;
• H. cooling said nonvolatile components to form a uniformly pigmented powder.

A method of preparing a powder paint composition comprising:

• A. polymerizing glycidyl acrylate or glycidyl methacrylate with an ethylenically unsaturated monomer in an inert solvent in such proportions as to obtain a copolymer with a glass transition temperature in the range of 40.degree. C to 90.degree. C and a number average molecular weight in the range of 2500 to 8500;
• B. introducing a flow control agent having a number average molecular weight of at least 100 into said copolymer solution;
• C. introducing pigment into said copolymer solution;
• D. passing a solution comprising the ingredients of (A), (B), and (C) through an evaprating zone comprising a tortuous path of relatively narrow cross-section, elongated in a direction lateral to the direction of flow of said solution through said zone;
• E. heating said solution while it is confined within said evaporating zone to a temperature
• 1. above the melting point of said copolymer, but below the point at which degradation occurs;
• 2. above the temperature at which said inert solvent begins to vaporize
• thus inducing turbulent flow of said solution within said evaporating zone and thereby maintaining an intimate homogeneous mixture of the vapors of the volatile components of said solution and the dispersed particles of nonvolatile components of said solution;
• F. passing said homogeneous mixture from said evaporating zone into a separating zone and, while maintaining the temperature within said separating zone at the same level as in (D), causing said solvent vapor to be removed and allowing said nonvolatile components to collect in a molten state;
• G. removing said nonvolatile components from said separating zone;
• H. cooling said nonvolatile components to form a solid material;
• and
• I. pulverizing said solid material to form a uniformlypigmented powder.