Friction-activatable adhesive and articles thereof
AssigneeMinnesota Mining and Manufacturing Company
InventorsWayne A. Pletcher, Roy Wong
Life of this patent
Estimating the term…
Abstract
A friction-activatable adhesive composition comprising a mixture of a crystallizable linear polyester, a tackifier and, optionally, a plasticizer therefor and adhesive sticks prepared from the adhesive compositions.
Claims12
A friction-activatable solvent-free adhesive composition comprising a mixture of
- 1. 25 to 95 parts by weight of a thermoplastic linear polyester having crystallizable ester units of the formula:
- ##STR2## wherein R.sub.1 consists of the divalent radical remaining after removal of the carboxyl groups from one or more saturated aliphatic dicarboxylic acids and/or aromatic dicarboxylic acids, R.sub.1 containing from 2 to 8 carbon atoms when it is an aliphatic radical and 6 to 13 carbon atoms when it is an aromatic radical, R.sub.2 consists of the divalent radical remaining after removal of the hydroxyl groups from one or more saturated aliphatic diols containing from 2 to 12 carbon atoms, said polyester having a DTA melting temperature of from about 40.degree. to 75.degree. C. and an inherent viscosity of at least 0.2 dl/g at 25.degree. C., as measured in a 0.5 g/dl solution of polymer in chloroform at 25.degree. C.,
- 2.
5 to 50 parts by weight of a low molecular weight thermoplastic resin tackifier for the polyester selected from hydrocarbon resins, reaction products of hydroabietyl alcohol and toluene diisocyanate, bituminous asphalts, coal tar pitches, rosins, phenolic resins, chlorinated aliphatic hydrocarbon waxes and chlorinated polynuclear aromatic hydrocarbons, the phenolic resins being reaction products of one or more members of the class consisting of phenol itself, cresols, xylenols, p-tert-butylphenol and p-phenylphenol with one or more members of the class consisting of formaldehyde, acetaldehyde and furfuraldehyde, said tackifier having the ability to lower the melting temperature of the polyester and to raise its glass transition temperature,
- 3.
An adhesive applicator stick comprising a mixture of
- 1. 25 to 95 parts by weight of a thermoplastic linear polyester having crystallizable ester units of the formula ##STR3## wherein R.sub.1 consists of the divalent radical remaining after removal of the carboxyl groups from one or more saturated aliphatic dicarboxylic acids and/or aromatic dicarboxylic acids, R.sub.1 containing from 2 to 8 carbon atoms when it is an aliphatic radical and 6 to 13 carbon atoms when it is an aromatic radical, R.sub.2 consists of the divalent radical remaining after removal of the hydroxyl groups from one or more saturated aliphatic diols containing from 2 to 12 carbon atoms, said polyester having a DTA melting temperature of from about 40.degree. to 75.degree. C. and an inherent viscosity of at least 0.2 dl/g at 25.degree. C., as measured in a 0.5 g/dl solution of polymer in chloroform at 25.degree. C.,
- 2. 5 to 50 parts by weight of a low molecular weight thermoplastic resin tackifier for the polyester selected from hydrocarbon resins, reaction products to hydroabietyl alcohol and toluene diisocyanate, bituminous asphalts, coal tar pitches, rosins, phenolic resins, chlorinated aliphatic hydrocarbon waxes and chlorinated polynuclear aromatic hydrocarbona, the phenolic resins being reaction products of one or more members of the class consisting of phenol itself, cresols, xylenols, p-tert-butylphenol and p-phenylphenol with one or more members of the class consisting of formaldehyde, acetaldehyde and furfuraldehyde, said tackifier having the ability to lower the melting temperature of the polyester and to raise its glass transition temperature,
- 3. 0 to 25 parts by weight of a plasticizer for the polyester selected from phthalates, phosphates and hydroabietyl alcohol, said plasticizer having the ability to lower the melting temperature and glass transition temperature of the polyester and to reduce its cohesive strength, the sum of (1), (2) and (3) being 100 parts by weight, said mixture being compatible and having
- a. a softening temperature of at least about 40.degree. C.,
- b. a write on factor of at least about 0.06,
- c. an open time of from about 1/3 to about 10 minutes,
- d. peel adhesion in the open state of not less than about 50 grams per centimeter, and
- e. peel adhesion in the closed state of not less than about 100 grams per centimeter.
Dependencies are inferred from the claim text.