Cadmium diffused Pb.sub.1-x Sn.sub.x Te diode laser

A method of making a higher power, more tunable lead-tin telluride infrared laser, said method comprising:

• placing a body of low dislocation density monocrystalline P-type semiconductive material in a chamber to receive cadmium as an N-type conductivity determining diffusion, said monocrystalline body having a (100) crystal plane and a surface parallel thereto, said semiconductive material having the composition Pb.sub.1-x Sn.sub.x Te with x being a value from zero to about 30 mol percent that is selected to provide a band gap corresponding to a photon of infrared radiation of a predetermined wavelength within a range of 6.5 - 32 microns;
• placing in said chamber a quantity of cadmium that is equal to about 0.05 - 0.08 milligrams of cadmium per cubic centimeter of chamber volume;
• closing said chamber while it is evacuated to a pressure no greater than about 1 .times. 10.sup.-6 Torr;
• heating said closed chamber at a preselected rate of about 100.degree. - 200.degree. C. per hour to a diffusion temperature of about 400.degree. - 500.degree. C.;
• maintaining said diffusion temperature for a preselected duration of the order of about 1 hour to diffuse cadmium into said body surface and form a planar, high injection efficiency PN junction in said body that is parallel to and at a preselected depth below said surface;
• cooling said body in said closed chamber from said diffusion temperature at a preselected rate of about 100.degree. - 200.degree. C. per hour to a temperature of about 150.degree. C.;
• cooling said body to room temperature at any rate, and removing it from said closed chamber at any time, after said body has been cooled to about 150.degree. C. in said chamber;
• contouring and polishing said body into a parallelepiped that has a laser cavity adjacent said PN junction for collecting and amplifying infrared radiation of said predetermined wavelength;
• applying ohmic contacts to said body by which a voltage can be applied across said PN junction to generate said infrared radiation of predetermined wavelength for collection and amplification in said laser cavity;
• and
• placing said parallelepiped in intimate thermal communication with cooling means for removing heat produced during generation, collection and amplification of said infrared radiation.

A method of making a higher power, more tunable lead-tin telluride infrared laser, said method comprising:

• polishing opposite surfaces of an elongated low dislocation density monocrystalline P-type semiconductive material parallel to its (100) crystal plane to form flat and parallel opposite surfaces on said body spaced about 400 - 600 micrometers apart, said semiconductive material having the composition Pb.sub.1-x Sn.sub.x Te with x being a value from zero to about 8 mol percent that is selected to provide a band gap corresponding to a photon of infrared radiation of a predetermined wavelength within a range of 6.5 - 9 microns and having a tellurium content up to 0.01 mol percent in excess of 50 mol percent to induce said P-type conductivity;
• placing said body in a chamber for receiving cadmium as and N-type conductivity determining diffusant;
• placing in said chamber a quantity of cadmium that is equal to about 0.06 - 0.07 milligrams of cadmium per cubic centimeter of chamber volume;
• sealing said chamber while it is evacuated to a pressure no greater than about 1 .times. 10.sup.-6 Torr;
• heating said sealed chamber at a preselected rate of the order of about 100.degree. C. per hour to a diffusion temperature of about 400.degree. - 500.degree. C.;
• maintaining said diffusion temperature for a preselected duration up to about 1/2 - 11/2 hours to diffuse cadmium into both of said opposite surfaces of said body and form a planar, high injection efficiency PN junction in said body that is parallel to said surfaces and at a preselected depth, within a range of 20 - 100 micrometers, below said surfaces;
• cooling said body in said sealed chamber from said diffusion temperature at a preselected rate of the order of 100.degree. C. per hour to a temperature of about 150.degree. C.;
• cooling said body to room temperature at any rate, and removing it from said chamber at any time, after said body has been cooled to about 150.degree. C. in said chamber;
• polishing one of said opposite surfaces of said body to remove its cadmium diffusion layer and reduce body thickness to less than about 250 micrometers;
• cleaving said body along said (100) crystal planes perpendicular to said opposite surfaces to form an elongated parallelepiped less than about 200 micrometers wide and about 300 - 600 micrometers long;
• polishing end surfaces of said elongated parallelepiped body to a reflective surface finish to form a laser cavity about 250 - 500 micrometers long adjacent said PN junction for collecting and amplifying said infrared radiation of predetermined wavelength;
• forming a discrete ohmic contact to each of said opposite surfaces of said body by which a voltage can be applied across said PN junction to generate said infrared radiation of predetermined wavelength for collection and amplification in said laser cavity;
• and
• soldering the parallelepiped body surface containing the remaining cadmium diffusion layer to a cooling member for removing heat produced in said body adjacent said PN junction during generation, collection and amplification of said infrared radiation.