US 4,064,620 AGranted

Ion implantation process for fabricating high frequency avalanche devices

AssigneeHughes Aircraft Company

InventorsDon H. Lee, Kenneth P. Weller, Robert S. Ying, William F. Thrower

Life of this patent

Estimating the term…

Loading patent…

Abstract

Disclosed are new high frequency ion implanted passivated semiconductor devices and a planar fabrication process therefor wherein initially an ion implantation and PN junction passivation mask is formed on one surface of a semiconductor crystal. Thereafter, one or more conductivity type determining ion species are implanted through an opening in the mask and into the semiconductor crystal to form active device regions including a PN junction, all of which are bounded by an annular, higher resistivity unimplanted region of the semiconductor crystal. The PN junction thus formed terminates beneath the implantation and passivation mask, and the semiconductor crystal is then annealed to remove ion implantation damage and to electrically activate the ion implanted regions, while simultaneously controlling the lateral movement of the PN junction beneath the passivation mask. Such annealing does not adversely affect the conductivity and passivation characteristics of either the higher resistivity annular region or the passivation mask, and the resultant device structure exhibits a small degradation in high frequency performance relative to comparable state of the art unpassivated devices. Devices fabricated with the present new passivated geometry have a structure with sufficient mechanical strength to allow direct mounting into high frequency circuits (of the microwave waveguide-cavity type) without the use of additional package arrangements.

Claims7

Dependent claims

A planar process for fabricating high frequency impact avalache transit time (IMPATT) devices having precisely controlled parasitic loss parameters and with structural characteristics which allow direct mounting into a microwave cavity, including the steps of:

a. forming a relatively thick insulating mask on the surface of a semiconductor crystal composed of a substrate of one conductivity type and a layer of said one conductivity type disposed thereon and of higher resistivity than said substrate.
b. implanting one or more ion species of said one conductivity type through an opening in said mask and into a central region of said crystal and thru said layer to thereby leave said central region of said crystal surrounded by a higher resistivity annular region
c. implanting further ion species through said opening in said mask and into said central region of said crystal to thereby form a planar PN junction terminating beneath said mask at the surface of said crystal,
d. annealing said semiconductor crystal to a predetermined elevated temperature sufficient to remove substantial amounts of ion implantation damage in said crystal and to electrically activate the ion implanted regions thereof,
e. depositing a layer of contact metalization on said insulating mask and extending into an opening thereof and into electrical contact with said central region of said semiconductor crystal,
f. bonding a heat sink to said contact metalization whereby said heat sink is in close proximity to said central region for providing a maximum of heat transfer therefrom, and portions of said contact metalization and heat sink remote from said central region are separated from said semiconductor crystal by the thickness of said relatively thick insulating mask which minimizes the capacitance and maximizes the resistance between said semiconductor crystal and said heat sink and thus minimizes microwave losses in said devices, and
g. removing a predefined portion of a region of said semiconductor crystal surrounding said central region and also removing a predefined portion of a region of said insulating mask surrounding the contact metalization making electrical contact with said central region to further minimize microwave losses in said devices and improve the high frequency performance thereof.

4 more elements

A planar process for fabricating high frequency impact avalanche trasit time (IMPATT) devices in a semiconductor structure comprising the steps of:

a. forming an epitaxial semiconductor layer on the surface of a semiconductor substrate and of higher resistivity than said substrate,
b. forming a relatively thick insulating mask on the surface of said epitaxial layer,
c. implanting ions of one conductivity type through an opening in said mask and into and thru a central region of said epitaxial layer, leaving the ion implanted central region surrounded by an annular region of said epitaxial layer of higher resisitivity than said central region,
d. introducing opposite conductivity type impurities into said central region to thereby form a PN junction which terminates at the surface of said epitaxial layer and beneath said insulating mask,
e. annealing the crystal structure of step (d) at a predetermined elevated temperature sufficient to remove substantial amounts of ion implantation damage in said semiconductor crystal structure and to electrically activate the ion implanted regions therein without adversely affecting the passivation and current limiting characteristics of either said insulating mask or said epitaxial layer,
f. depositing a layer of contact metalization on said insulating mask and extending into an opening thereof and into electrical contact with said central region of said semiconductor crystal,
g. bonding a heat sink to said contact metalization whereby said heat sink is in close proximity to said central region for providing a maximum of heat transfer therefrom, and portions of said contact metalization and heat sink remote from said central region are separated from said semiconductor crystal by the thickness of said insulating mask which maximizes the resistance and minimizes the capacitance between said semiconductor crystal and said heat sink and thus minimizes microwave losses in said devices, and
h. removing a predefined portion of a region of said semiconductor crystal surrounding said central region and also removing a predefined portion of a region of said insulating mask surrounding the contact metalization making electrical contact with said central region to further minimize microwave losses in said devices and improve the high frequency performance thereof.

5 more elements

A planar process for fabricating high frequency ion implanted microwave devices in a semiconductor crystal including the steps of:

a. forming an epitaxial layer of N.sup.- semiconductive material on an N.sup.+ semiconductor substrate to thereby form an N.sup.+ -N.sup.- interface in a monocrystalline semiconductor body,
b. forming a relatively thick insulating mask on the surface of said N.sup.- epitaxial layer,
c. implanting N type ions through an opening in said mask and into said epitaxial layer with a projected range, R.sub.p, located approximately at said N.sup.+ -N.sup.- interface and defining a central ion implanted region of said epitaxial layer,
d. introducing P type impurities into said central region to thereby form a PN junction therein terminating beneath said insulating mask,
e. annealing the ion implanted crystal in step (d) above to a predetermined elevated temperature sufficient to remove a substantial amount of ion implantation damage within said semiconductor crystal and to electrically activate said ion implanted regions therein,
f. depositing a layer of contact metalization on said insulating mask and extending into an opening thereof and into electrical contact with said central region of said semiconductor crystal,
g. bonding a heat sink to said contact metalization whereby said heat sink is in close proximity to said central region for providing a maximum of heat transfer therefrom, and portions of said contact metalization and heat sink remote from said central region are separated from said semiconductor crystal by the thickness of said insulation mask which maximizes the resistance and minimizes the capacitance between said semiconductor crystal and said heat sink and thus minimizes microwave losses in said devices, and
h. removing a predefined portion of a region of said semiconductor crystal surrounding said central region and also removing a predefined portaon of a region of said insulating mask surrounding the metalization making electrical contact with said central region to further minimize microwave losses in said devices and improve the high frequency performance thereof.

5 more elements