Refractory linings

A slag resistant refractory lining material consisting of 75 parts by weight of corundum screened below 6 mm, 10 parts by weight of refractory clay screened below 1.0 mm, 15 parts by weight of silicon carbide screened below 0.15 mm and an additional 5 parts by weight of a 40 percent water suspension of colloidal silica.

A slag resistant refractory lining material consisting essentially of refractory grains of silicon carbide screened below 6 mm, and from 2 to 15 percent by weight of the total solids content of a binder selected from the group consisting of bond clay, aluminate, and chromate cements, phosphoric acid, spent sulphite liquor and carboxymethyl cellulose, and containing an additional amount of water suspension colloidal silica in a quantity corresponding to 0.4 - 4% SiO.sub.2 by weight of the solids content of the lining material and further containing a carbonaceous material selected from the group consisting of coke, graphite, pitch, and silicon carbide, screened below 1 mm.

A slag resistant refractory lining material comprising 45 parts calcined fire-clay screened below 6 mm, 45 parts clay screened below 1 mm, 10 parts graphite powder, and 5 parts of a 40% suspension of colloidal silica.

A slag resistant refractory lining material comprising 90 parts magnesite screened below 6 mm, 10 parts pitch screened below 1 mm, 2 parts magnesium sulphate dissolved in water, and 5 parts of a 40% suspension of colloidal silica.