Biaxially oriented polyethylene terephthalate film and method of making such film

A method of making biaxially oriented polyethylene terephthalate film including the steps of:

• stretching amorphous polyethylene terephthalate film heated to a temperature slightly above its glass temperature in a first direction about 1.2 to 2 times its initial length to orient it uniaxially;
• heating such uniaxially oriented film to a stabilizing temperature from about 100.degree. to 105.degree. C in a tenter frame without stretching after it has been stretched in the first direction and before it is stretched in a second direction;
• thereafter, cooling the film to a temperature substantially the same as the first temperature;
• stretching the film in the second direction in the tenter frame about 3 to 4 times its width before stretching to orient it in that direction;
• and
• cooling the film below its stretching temperature after stretching in the second direction in the tenter frame whereby such film has a shrinkage, on heating to 100.degree. C for 5 seconds, of less than 8% in the first direction and greater than 40% in the second direction.

A method of making biaxially oriented polyethylene terephthalate film including the steps of:

• stretching amorphous polyethylene terephthalate film in the machine direction (MD) at a temperature and rate whereby such film has a MD shrinkage, on heating to 100.degree. C. for 5 seconds, of between 30% to 50%;
• thereafter subjecting the thus stretched film to a temperature higher than the MD stretching temperature while the film is under restraint whereby such film has an MD shrinkage, on heating to 100.degree. C. for 5 seconds, of less than 8%;
• and
• thereafter stretching the thus heated film in the cross-machine direction (TD) at a temperature and rate whereby such film has a TD shrinkage, on heating to 100.degree. C. for 5 seconds, of greater than 40%.

A method of making heat-shrinkable, heat-sealable polyethylene terephthalate film including the steps of:

• stretching amorphous polyethylene terephthalate film in a machine direction about 1.2 to 2 times its initial length at a temperature from slightly above its glass transition temperature to 25.degree. C. above such glass transition temperature;
• heating such stretched film to an intermediate temperature higher than the temperature of the MD stretching temperature while restraining the film from the shrinkage by engaging it along its edges whereby to relax the stretched film;
• stretching such relaxed film in a cross-machine direction while heating it to a temperature lower than the intermediate temperature and stretching it to about 3 to 4 times its width before stretching;
• and
• cooling the film rapidly to a temperature below its glass transition temperature.

A method of making heat-sealable, heat-shrinkable, biaxially oriented polyethylene terephthalate film including the steps of:

• stretching an amorphous polyethylene terephthalate film of a viscosity of at least 0.5 in the machine direction from 1.5 to 2.0 times its initial length at a temperature from between about 78.degree. to 95.degree. C.;
• engaging the thus stretched film in the clips of a tenter chain in a tenter frame;
• subjecting the film to a temperature of from 100.degree. C. to 105.degree. C. without stretching;
• thereafter stretching the film in a cross-machine direction in the tenter frame from 3.2 to 3.5 times its width after machine direction stretching at a temperature from between about 82.degree. to 92.degree. C.;
• and
• immediately cooling the then stretched film below 78.degree. C. without stretching or relaxation.

A method of making biaxially oriented polyethylene terephthalate film including the steps of:

• casting polyethylene terephthalate film onto a quenching surface;
• forming amorphous polyethylene terephthalate film on such surface;
• stripping such amorphous polyethylene terephthalate film from such surface, such amorphous polyethylene terephthalate film having a viscosity of at least 0.55;
• stretching such amorphous film from 1.5 to 2 times its initial length while such film is at a temperature of between about 88.degree. to 90.degree. C.;
• engaging the thus stretched film in the clips of a tenter chain in a tenter frame;
• heating the film to a temperature of from about 100.degree. C. to 105.degree. C. for approximately 5 seconds without stretching while in the tenter frame;
• thereafter stretching the film transversely in the tenter frame from 3.2 to 3.5 times its width while such film is at a temperature of between about 88.degree. and 90.degree. C.;
• and
• cooling the film below 78.degree. C. without stretching or relaxation.