Process for preparing wholly aromatic polyamides by mixing solid particulate reactants and polymerizing
AssigneeCelanese Corporation
InventorRufus S. Jones, Jr.
Life of this patent
Estimating the term…
Abstract
An improved process is provided for preparing wholly aromatic polyamides from solid monomers; particularly, aromatic diamines and aromatic dicarboxylic acid halides. The solid monomers in particulate form are first mixed in the substantial absence of oxygen and in the absence of a solvent or diluent to prepare a uniform monomer mixture having a desired stoichiometry prior to the initiation of the polymerization reaction. The uniform monomer mixture is thereafter polymerized in the presence of an appropriate solvent as herein defined.
Claims11
A process for the preparation of a wholly aromatic polyamide from an aromatic diamine and an aromatic diacid halide comprising:
- a. mixing solid particulate diamine and solid particulate aromatic diacid halide in the substantial absence of oxygen and in the absence of a solvent or diluent therefor to obtain a uniform stoichiometrically balanced solids mixture;
- and
- b. thereafter polymerizing the resulting uniform solids mixture in an amide solvent to obtain said wholly aromatic polyamide having an inherent viscosity of at least above about 0.7 to about 6.0, said inherent viscosity being measured on a solution of 0.4 grams of polyamide per 100 cc. of cencentrated H.sub.2 SO.sub.4 at 25.degree. C.
A process for the preparation of a wholly aromatic polyamide which comprises:
- a. mixing, in about an equimolar ratio, a solid aromatic diamine of the formula H.sub.2 N--Ar--NH.sub.2 and a solid aromatic diacid halide of the formula ##STR11## wherein Ar is a divalent aromatic radical which is meta or para oriented and which is selected from the group consisting of ##STR12## wherein R is alkyl or alkoxy of 1 to 6 carbons, chlorine, bromine or phenyl;
- n is an integer of 0 to 4;
- and X is --O--, --S--, ##STR13## --C--, alkenylene of 2 to 6 carbons, cycyloalkylidene of up to 8 carbons, azo, azoxy, or ##STR14## wherein Y.sub.1 and Y.sub.2 are independently hydrogen, alkyl of 1 to 6 carbons, phenyl or substituted phenyl;
- and Hal is chlorine or bromine, to obtain a uniform stoichiometrically balanced solids mixture, and
- b. thereafter polymerizing the resulting uniform solids mixture in an amine solvent selected from the group consisting of compounds of the formula ##STR15## wherein R.sup.1 is hydrogen or alkyl of 1 to 4 carbons and R.sup.2 and R.sup.3 are alkyl of 1 to 4 carbons;
- tetramethylurea;
- N-methyl pyrrolidone and hexamethylphosphoramide, for a time sufficient to obtain a wholly aromatic polyamide having an inherent viscosity of from about 1.0 to about 6.0, said inherent viscosity being measured on a solution of 0.4 grams of polyamide per 100 cc. of concentrated H.sub.2 SO.sub.4 at 25.degree. C.
Dependencies are inferred from the claim text.