Process for the preparation of terpene-phenol resins by three-stage reaction of phenol with carene using Friedel-Crafts or Lewis acid catalyst
AssigneeLes Derives Resiniques et Terpeniques
InventorsBernard Lahourcade, Gustave Bonneau
Life of this patent
Estimating the term…
Abstract
This invention relates to a process for the preparation of improved terpene-phenol resins particularly useful in the field of adhesives, comprising: A. reacting 1 molar proportion of a phenol having at least 2 reactive sites with 0.4-0.6 molar proportion of a carene, in the presence of an acidic condensation catalyst; B. reacting the reaction product obtained in step (a) with 0.4-0.6 molar proportion of said carene in the presence of said catalyst, and C. subsequently reacting the material obtained in step (b) with a reactive terpene, the molar ratio between said reactive terpene and the amount of carene added in step (b) being comprised between 0.5 and 5.
Claims8
Process for the preparation of terpene-phenol resins by reaction of a carene with a phenol in the presence of an acidic condensation catalyst, comprising:
- a. reacting at a temperature of 80.degree.-120.degree. C one molar proportion of a phenol having at least two reactive sites with 0.4-0.6 molar proportion of a carene, in the presence of an acidic condensation catalyst selected from a Lewis acid type catalyst and a Friedel-Crafts type catalyst:
- b. reacting at a temperature of 80.degree.-120.degree. C the reaction product from step (a) with 0.4-0.6 molar proportion of said carene, in the presence of said catalyst, said carene being added in steps (a) and (b) at a temperature of 20.degree.-100.degree. C;
- and
- c. subsequently reacting at a temperature of 80.degree.-120.degree. C the product from step (b) with a reactive terpene, the molar ratio of reactive terpene to amount of carene added in step (b) being comprised within the range from 0.5 to 5;
- steps (a)-(c) being carried out under an inert gaseous atmosphere and in the presence of an aromatic hydrocarbon solvent;
- thereby obtaining a terpene-phenol resin of clear stable color having a Ring and Ball melting point range of 95.degree.-98.degree. C.
Dependencies are inferred from the claim text.