Process for producing an improved dielectrically-isolated silicon crystal utilizing adjacent areas of different insulators
AssigneeFairchild Camera and Instrument Corporation
InventorRobert J. Kopp
Life of this patent
Estimating the term…
Abstract
Thermoprocessing of integrated-circuit devices and ionizing radiation environments create electronic charges in dielectric isolation materials and in dielectric-semiconductor interface regions. These charges can produce serious alterations in the operating characteristics of the devices and integrated circuits. The deleterious effect of these charges may be greatly reduced by the disclosed process which produces a single-crystal silicon film dielectrically isolated from a polycrystalline silicon support by an underlying insulator of either silicon nitride or silicon dioxide, both of which may be grown by the process at selected locations on the same chip.
Claims9
A method for fabricating single-crystal silicon films dielectrically isolated from each other and from a common substrate by silicon dioxide and silicon nitride insulating films, said method comprising the steps of:
- epitaxially growing a silicon film to a thickness of approximately four micrometers on the surface of a heavily-doped n-type single-crystal silicon wafer;
- coating the surface of said silicon film with a first dielectric material to a thickness of approximately 0.2 micrometers;
- masking all portions of the surface of said first dielectric material that are to be retained for dielectric isolation and removing all portions of said first dielectric material that are not masked and are to be isolated by a second dielectric material;
- coating the areas on the surface of said silicon film that have been exposed by the removal of portions of said first dielectric material with a second dielectric material;
- depositing on the exposed surfaces of said first and second dielectric materials a relatively thick supporting layer of polycrystalline silicon;
- removing said heavily-doped n-type silicon wafer by electrochemically etching it from said epitaxially-grown silicon film;
- vapor thinning said silicon film to a desired thickness;
- and
- selectively etching through said silicon film to form individual single-crystal device islands on said first and second dielectric materials.