Barium titanate ceramic
AssigneeNGK Insulators, Ltd.
InventorsShigetaka Wada, Senji Atsumi
Life of this patent
Estimating the term…
Abstract
A ceramic is disclosed which maintains a high electric resistance over a wide temperature range and has a large temperature coefficient of resistance variation at temperatures just below the aforesaid range, the PTC ceramic consisting essentially of 100 parts by weight of four ingredients including A. 1 mol of barium titanate composition, B. 0.003 to 0.05 mol of titania, C. 0.003 to 0.05 mol of alumina, and D. 0.005 to 0.06 mol of silica; 0.05 to 0.3 part by weight of E. tantalum pentoxide and/or antimony pentoxide; and 0.005 to 0.03 part by weight of F. manganese and/or copper.
Claims12
A ceramic having a positive temperature coefficient of electric resistance, consisting essentially of:
- 100 parts by weight of four ingredients including
- a. 1 mol of one barium titanate composition which is selected from the group consisting of barium titanate, 0.0001 to 0.35 mol of lead titanate and the remainder of barium titanate, 0.0001 to 0.4 mol of strontium titanate and the remainder of barium titanate, and 0.0001 to 0.15 mol of barium stannate and the remainder of barium titanate,
- b. 0.003 to 0.05 mol of titania,
- c. 0.003 to 0.05 mol of alumina, and
- d. 0.005 to 0.06 mol of silica;
- 0.05 to 0.3 part by weight of at least one oxide selected from the group consisting of tantalum pentoxide and antimony pentoxide based on the preceding 100parts by weight of ingredients (a) to (d);
- and
- 0.005 to 0.03 part by weight of at least one metal selected from the group consisting of manganese and copper based on the preceding 100 parts by weight of ingredients (a) to (d).
A ceramic having a positive temperature coefficient of electric resistance, consisting essentially of:
- 100 parts by weight of four ingredients including
- a. 1 mol of one barium titanate composition which is selected from the group consisting of barium titanate, 0.0001 to 0.35 mol of lead titanate and the remainder of barium titanate, 0.0001 to 0.4 mol of strontium titanate and the remainder of barium titanate, and 0.001 to 0.15 mol of barium stannate and the remainder of barium titanate,
- b. 0.01 to 0.03 mol of titania,
- c. 0.005 to 0.25 mol of alumina, and
- d. 0.01 to 0.04 mol of silica;
- 0.1 to 0.2 part by weight of at least one oxide selected from the group consisting of tantalum pentoxide and antimony pentoxide based on the preceding 100 parts by weight of ingredients (a) to (d);
- and
- 0.01 to 0.02 part by weight of at least one metal selected from the group consisting of manganese and copper based on the preceding 100 parts by weight of ingredients (a) to (d).
Dependencies are inferred from the claim text.