Process for improving the adhesion of hot melts to metal substrates
AssigneeMonsanto Company
InventorDonald D. Donermeyer
Life of this patent
Estimating the term…
Abstract
Adhesion of filled poly(ester-amide) adhesive compositions to metal substrates is improved by priming the metal substrate with a tie coat of an etherified methylolmelamine prior to application of the filled poly(ester-amide). The etherified methylolmelamine is the condensation product of melamine, formaldehyde and an alkanol or cycloalkanol in which the degree of methylolation is in the range of about 5 to 6, the degree of etherification is in the range of about 3 to 6 and the degree of methylation is at least about 2.
Claims16
A process for adhering a filled copoly(esteramide) to a metal substrate which comprises:
- a. applying to the metal substrate a primer comprising an etherified methylolmelamine with a degree of methylolation in the range of about 5 to 6, a degree of etherification with a C.sub.1 to C.sub.6 alkanol or cycloalkanol in the range of about 3 to 6, and a degree of methylation of at least about 2 to provide a coating weight in the range of 1 to 166 g. per sq. meter;
- b. heating the substrate to a temperature in the range of about 150.degree. to about 300.degree. C. to convert the etherified methylolmelamine from the liquid to the solid state;
- and
- c. applying the filled copoly(ester-amide) as a hot melt to the formed surface at a temperature in the range of about 150.degree. to 300.degree. C.
A coated article comprising a metal substrate, a primer and a filled copoly(ester-amide);
- wherein the primer is a liquid etherified methylolmelamine with a degree of methylolation in the range of about 5 to 6, a degree of etherification with a C.sub.1 to C.sub.6 alkanol or cycloalkanol in the range of about 3 to 6, and a degree of methylation of at least about 2, which has been applied to provide a coating weight in the range of 1 to 166 g. per sq. meter and advanced to the solid state.
A coated article comprising a metal substrate, a primer and a filled copoly(ester-amide);
- wherein the primer comprises an etherified methylolmelamine with a degree of methylolation in the range of about 5 to 6, a degree of etherification with a C.sub.1 to C.sub.6 alkanol or cycloalkanol in the range of about 3 to 6, and a degree of methylation of at least about 2, which has been applied to provide a coating weight in the range of 1 to 166 g. per sq. meter and advanced to the solid state;
- and wherein the filled copoly(ester-amide) comprises:
- a. from about 70 to about 30 parts by weight of a poly(ester-amide) block copolymer of inherent viscosity in the range of about 0.35 to about 0.95 and of melting point in the range of about 155.degree. to about 225.degree. C., having from about 30 to about 70 percent by weight of crystalline polyester segments selected from the group consisting of poly(ethylene-terephthalate), co-poly(butylene terephthalate)-(ethylene terephthalate), co-poly(ethylene-terephthalate)-(ethylene isophthalate) and co-poly(ethylene terephthalate)-(propylene terephthalate which prior to incorporation in the poly(ester-amide), have an inherent viscosity in the range of about 0.05 to about 0.70 and a melting point in the range of about 180.degree. to about 270.degree. C., and from about 70 to about 30 percent by weight of amorphous polyamide segments derived from a C.sub.36 dibasic acid and analiphatic or alicyclic diamine containing from 2 to 10 carbon atoms, the inherent viscosity being determined at 25.degree. C. with an 0.5 gram solution in 100 ml. of a solvent mixture of 60 parts by weight of phenol and 40 parts by weight of symm-tetrachloroethane;
- and
- b. from about 30 to about 70 parts by weight of spheroidal aluminum powder of particle size in the range of about 4 to about 100 microns.
Dependencies are inferred from the claim text.