Preparation of films and coatings of para ordered aromatic heterocyclic polymers
AssigneeThe United States of America as represented by the Secretary of the Air Force
InventorsThaddeus E. Helminiak, Fred E. Arnold
Life of this patent
Estimating the term…
Abstract
Films and coatings are prepared from a dispersion of microscopic sheets of para ordered aromatic heterocyclic polymers by collecting the sheets from the dispersion either by filtration on a porous surface or by drawing a metal surface through the dispersion, and allowing the dispersion medium to evaporate. Upon drying the microscopic sheets coalesce to form the films or coatings. This procedure makes possible the fabrication of high quality, thermally stable films and coatings without the use of high temperature cures or other severe conditions.
Claims10
A method of fabricating a composite film consisting of a para ordered aromatic heterocyclic polymer having the following formula:
- --Z-Ar].sub.n,
- where Z is a heterocyclic selected from the group consisting of ##STR5## where Ar is ##STR6## and n is an integer having a value such that the polymer has an inherent viscosity of at least 2, said method comprising the following steps:
- a. mixing a solution consisting of the polymer in a solvent therefor wth a non-solvent for the polymer having a boiling point up to about 100.degree. C and being selected from the group consisting of a hydrocarbon and an alcohol, the amount of non-solvent mixed with the solution being sufficient to precipitate the polymer from solution, thereby precipitating the polymer in the form of two dimensional, microscopic sheets;
- b. separating the microscopic sheets from the resulting mixture while maintaining the sheets wetted with the non-solvent;
- c. mixing the wetted microscopic sheets with the non-solvent so as to provide a dispersion containing about 0.1 to 5 grams of the sheets per 100 milliliters of non-solvent;
- d. collecting from the dispersion at least one layer of the microscopic sheets;
- and
- e. evaporating non-solvent from the sheets so that they coalesce and form a composite film.
As an article of manufacture, a composite film comprising at least one layer consisting of two dimensional, microscopic sheets of a para ordered aromatic heterocyclic polymer, the sheets being coalesced to one another to form the film, said polymer having the following formula:
- --Z-Ar].sub.n,
- where Z is a heterocyclic selected from the group consisting of ##STR12## where Ar is ##STR13## and n is an integer having a value such that the polymer has an inherent viscosity of at least 2.
Dependencies are inferred from the claim text.