Catalytic hydrocarbon reforming process and catalyst
AssigneeContinental Oil Company
InventorWilliam Ralph Beaty, Jr.
Life of this patent
Estimating the term…
Abstract
A process and catalyst for converting hydrocarbon oils to desirable components by contacting said oils in the presence of hydrogen under hydrocarbon conversion conditions with a catalyst comprising a catalytic amount of a catalytic metal supported on gamma alumina.
Claims13
A catalyst for hydrocarbon reforming consisting essentially of from about 0.01 to about 10 weight percent based on the catalyst weight of at least 1 catalytic metal selected from the group consisting of palladium, vanadium, platinum, rhenium and iridium, supported on a gamma alumina produced by a process consisting essentially of
- a. hydrolyzing aluminum alkoxides to produce an aqueous alumina portion containing up to about 32 weight percent Al.sub.2 O.sub.3 and an organic reaction product;
- b. contacting said aqueous alumina slurry with an organic solvent selected from the group consisting of ethanol, propanol, isopropanol, butanol, hexanol, isobutanol and tertiary butanol in an amount sufficient to produce alumina having a cumulative pore volume (0-10,000A) from about 1.0 to about 2.75 cc/g, a surface area from about 225 to about 400 m.sup.2 /g and a loose bulk density from about 7.5 to about 25 lb/ft.sup.3 upon drying to an Al.sub.2 O.sub.3 content from about 80 to about 100 weight percent to form a solvent-aqueous alumina mixture;
- c. drying said solvent-aqueous alumina mixture to produce alumina;
- and
- d. forming said alumina of (c) into particles and calcining to produce said gamma alumina.
A catalyst for hydrocarbon isomerization consisting essentially of from about 0.01 to about 10 weight percent on the catalyst weight of at least 1 catalytic metal selected from the group consisting of palladium, nickel, platinum, molybdenum, cobalt, and copper supported on gamma alumina produced by a process consisting essentially of
- a. hydrolyzing aluminum alkoxides to produce an aqueous alumina portion containing up to about 32 weight percent Al.sub.2 O.sub.3 and an organic reaction product;
- b. contacting said aqueous alumina slurry with an organic solvent selected from the group consisting of ethanol, propanol, isopropanol, butanol, hexanol, isobutanol and tertiary butanol in an amount sufficient to produce alumina having a cumulative pore volume (0-10,000A) from about 1.0 to about 2.75 cc/g, a surface area from about 225 to about 400 m.sup.2 /g and a loose bulk density from about 7.5 to about 25 lb/ft.sup.3 upon drying to an Al.sub.2 O.sub.3 content from about 80 to about 100 weight percent to form a solvent-aqueous alumina mixture;
- c. drying said solvent-aqueous mixture to produce alumina, and;
- d. forming said alumina of (c) into particles and calcining to produce said gamma alumina.
A process for reforming light hydrocarbon stocks at a hydrogen to hydrocarbon ratio of about 1:1 to about 20:1 respectively, at temperatures of from about 700.degree. to 1,000.degree. F and pressures of from about 100-1,000 pounds per square inch gauge with a catalyst consisting essentially of from about 0.1 to about 10 weight percent based on the catalyst weight of at least 1 catalytic metal selected from the group consisting of palladium, vanadium, platinum, rhenium, and iridium supported on gamma alumina produced by a process consisting essentially of;
- a. hydrolyzing aluminum alkoxides to produce an aqueous alumina slurry and an organic reaction product,
- b. contacting said aqueous alumina slurry with an organic solvent selected from the group consisting of ethanol, propanol, isopropanol, butanol, hexanol, isobutanol and tertiary butanol in an amount sufficient to produce alumina having a cumulative pore volume (0-10,000A) from about 1.0 to about 2.75 cc/g, a surface area from about 225 to about 400 m.sup.2 /g and a loose bulk density from about 7.5 to about 25 lb/ft.sup.3 and a loose bulk density from about 7.5 to about 25 lb/ft.sup.3 upon drying to an Al.sub.2 O.sub.3 content from about 80 to about 100 weight percent to form a solvent-aqueous alumina mixture,
- c. drying said solvent-aqueous alumina mixture to produce alumina, and
- d. forming said alumina into particles and calcining to produce said gamma alumina.
A process for isomerization of hydrocarbon oil by contacting said oil with hydrogen at a hydrocarbon to hydrogen ratio of about 0.2:1 to about 10:1 respectively, under conditions of from about 260.degree. to about 950.degree. F and a pressure of about 15 to about 1,000 pounds per square inch actual with a catalyst consisting essentially of about 0.1 to about 10 percent by weight based on the weight of the catalyst of a metal selected from the group consisting of palladium, platinum, molybdenum, nickel, cobalt, and copper supported on a gamma alumina produced by a process consisting essentially of:
- a. hydrolyzing aluminum alkoxides to produce an aqueous alumina slurry and an organic reaction product,
- b. contacting said aqueous alumina slurry with an organic solvent selected from the group consisting of ethanol, propanol, isopropanol, butanol, hexanol, isobutanol and tertiary butanol in an amount sufficient to produce alumina having a cumulative pore volume (0-10,000A) from about 1.0 to about 2.75 cc/g, a surface area from about 225 to about 400 m.sup.2 g and a loose bulk density from about 7.5 to about 25 lb/ft.sup.3 upon drying to an Al.sub.2 O.sub.3 content from about 80 to about 100 weight percent to form a solvent-aqueous alumina mixture,
- c. drying said solvent-aqueous alumina mixture to produce alumina, and
- d. forming said alumina into particles and calcining to produce said gamma alumina.