Treatment material and method for exposed aggregate concrete casting
OwnerRatanjit S. Sondheinventor
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
OwnerRatanjit S. Sondheinventor
Estimating the term…
There is disclosed a method of and composition for making exposed aggregate concrete castings which comprises applying a film to the face of the mold or form, comprising a chelating agent to prevent the setting of the cement to a pre-determined depth at the face, whereby the ultimate appearance of the casting is decorative and the removal of the matrix to produce such appearance is effected by water, the penetration of the compound into the face depending on the selection and concentration of various ingredients. A single film only is applied to the form, and the material from which the film is formed includes cellulose ethers, aliphatic hydroxy acid or salts thereof, and one or a mixture of the lower aliphatic alcohols selected from the group methanol, ethanol or iso-proponol or a ketone. A plasticizer is often used as well as an identifying dye.
A composition for preventing the setting of concrete comprising by weight from 3% to 10% of a film former dissolved in from 84.5% to 95% of an aliphatic alcohol having 1 to 3 carbon atoms, and from 2% to 5.5% of a chelating compound;
A composition for preventing the setting of concrete comprising by weight 6.22% hydroxy propyl cellulose dissolved in 87.08% methanol, 2.76% citric acid, 3.87% ethylene glycol and .06% polar dye.
A composition for preventing the setting of concrete comprising by weight 5% hydroxy propyl cellulose dissolved in 86% methanol, 5.5% of a chelating compound, 3% ethylene glycol, and 0.05% polar dye, wherein said chelating compound is selected from the group consisting of citric, tartaric, and gluconic acids, the sodium and calcium salts of these acids, and mixtures thereof.
A method of making a composition to prevent the setting of concrete which comprises dissolving from 3% to 10% of a film former in from 84.5% to 95% of an aliphatic alcohol having 1-3 carbon atoms and adding thereto from 2% to 5.5% of a chelating compound, and mixing slowly until the mixture is homogeneous, wherein the percentages are by weight based on the total composition being 100%, wherein said film former is a cellulose ether of the type which is soluble in both water and said aliphatic alcohol, and wherein said chelating compound is selected from the group consisting of citric, tartaric, and gluconic acids, the sodium and calcium salts of those acids, and mixtures thereof.