Method of producing low-carbon, white husk ash
AssigneeRefratechnik GmbH
InventorsAlexander Tutsek, Peter Bartha
Life of this patent
Estimating the term…
Abstract
Low carbon, white husk ash suitable for use in manufacturing building materials, more particularly refractory building materials are prepared by first removing volatile constituents by heating the husks, normally rice husks but alternatively, for example, wheat, oats or barley husks, to a first relatively low temperature below the ignition point of the husks. Fixed carbon is then oxidized in the presence of a reagent by heating the husks to a second temperature above the separation temperature but below the crystallization temperature of the SiO.sub.2 in the husks, following by a heat treatment at a third temperature above the crystallization temperature of the SiO.sub.2, to produce a uniform SiO.sub.2 crystal structure.
Claims7
In a method of producing low-carbon, white rice husk ash suitable for the production of building materials, and more particularly refractory building materials, in which method, for purposes of removing volatile constituents and for purposes of transforming the fixed carbon into a gaseous compound, the rice husks are heated to a temperature below the crystallization temperature of the SiO.sub.2 of the rice husks, whereupon the resultant husk ash is heat-treated at a temperature above the crystallization temperature of the SiO.sub.2 for the purposes of obtaining a uniform SiO.sub.2 crystal structure, the improvement comprising:
- the first step of heating the rice husks to a first relatively low separation temperature within the range of from 200.degree. to 450.degree. C. in the absence of air, exclusively for separating the volatile constituents that are capable of after-burning;
- subsequently the second step of heating the rice husks free of volatile constituents to a gasification temperature in the range of from 450.degree. to 550.degree. C. while feeding an oxidizing agent thereto for transforming the fixed carbon into a gaseous phase prior to heat treatment;
- and the third step of subsequently heating the thus obtained rice husk ash to a heat treatment temperature in the range of from 700.degree. to 800.degree. C.
Dependencies are inferred from the claim text.