High density urethane foam for rim
AssigneeMcCord Corporation
InventorWayne C. Salisbury
Life of this patent
Estimating the term…
Abstract
A highly reactive urethane foam for RIM to produce thin-sectioned automobile trim components having good high temperature sag performance is a quasi prepolymer system in which the polyol side is based on a relatively high molecular weight polyol combined with a known highly reactive unhindered aromatic polyamine chain extender/cross linker and with conventional short chain diols/triol extenders/cross linkers and catalysts.
Claims6
A polyurethane foam prepared by intimately mixing
- A. a polyol blend comprising (parts by weight):
- ______________________________________ long chain polyol 50 to 100 cross linker/extender 0 to 25 aromatic polyamine 1 to 6 alkylene amine catalyst 0.01 to 3.0 organometal catalyst 0.01 to 0.05 ______________________________________
- with
- B. a quasi prepolymer of an alkane diol and an aromatic diisocyanate, said quasi prepolymer having a free NCO in the range of 20 to 27 percent;
- wherein:
- said long chain polyol has a molecular weight in the range of 3000 to 6000, a functionality in the range of 2 to 3, and an equivalent weight of 1500 to 3000:
- said crosslinker/extender has a molecular weight in the range of 62 to 250 and is selected from the group consisting of alkane diols and triols;
- said aromatic polyamine has the formula ##STR2##
- and n has the value in the range of 0.1 to 0.7, and
- said polyol blend and said quasi prepolymer are admixed to an Index in the range of 98 to 106.
A polyurethane foam prepared by intimately mixing in a RIM system and reacting
- A. a polyol blend comprising (parts by weight):
- ______________________________________ long chain polyol 70 to 90 [alkane diol/triol #1 10 to 20] [alkane diol/triol #2 10 to 20] aromatic polyamine 3 to 4 alkylene amine catalyst 0.8 to 1.6 organometal catalyst 0.015 to 0.030 carbon black 0.01 to 1.0 gaseous blowing agent 3 to 8 ______________________________________
- and a crosslinker/extender blend comprising in the range of 10 to 20 parts of a first hydroxyl compound and 0.10 to 20 parts of a second hydroxyl compound different from said first hydroxyl compound, said hydroxyl compounds being selected from the group consisting of alkane diols and triols;
- with
- B. a quasi prepolymer of an alkane diol and an MDI, said quasi prepolymer having a free NCO in the range of 22 to 24 percent;
- wherein:
- said long chain polyol has a molecular weight in the range of 3000 to 6000, a functionality in the range of 2 to 3, and an equivalent weight of 1500 to 3000;
- all of said alkane diols and triols have a molecular weight in the range of 62 to 250;
- said aromatic polyamine has the formula ##STR3##
- and n has a value in the range of 0.1 to 0.7.
A method of making a thin-sectioned component of a polyurethane high density foam comprising injecting via a RIM machine into a mold cavity of the desired configuration a highly reactive quasi prepolymer foam formulation, allowing said formulation to cure in said mold cavity, and demolding the molded article in less than two minutes from the time of injection, said formulation being:
- A. a polyol blend comprising (parts by weight):
- ______________________________________ long chain polyol 50 to 100 cross linker/extender 0 to 25 aromatic polyamine 1 to 6 alkylene amine catalyst 0.01 to 3.0 organometal catalyst 0.01 to 0.05 ______________________________________
- with
- B. a quasi prepolymer of an alkane diol and an aromatic diisocyanate, said quasi prepolymer having a FNCO in the range of 20 to 27 percent;
- wherein:
- said long chain polyol has a molecular weight in the range of 3000 to 6000, a functionality in the range of 2 to 3, and an equivalent weight of 1500 to 3000,
- said crosslinker/extender has a molecular weight in the range of 62 to 250 and is selected from the group consisting of alkane diols and triols,
- said aromatic polyamine has the formula ##STR4##
- and n has a value in the range of 0.1 to 0.7;
- and said polyol blend and said quasi prepolymer are admixed to an Index in the range of 98 to 106.
A method of making a thin-sectioned automobile trim component of a polyurethane high density foam comprising injecting via a RIM machine providing a time from initial mixing to injection of less than 0.01 seconds into a mold cavity of the desired configuration a highly reactive quasi prepolymer foam formulation, allowing said formulation to cure in said mold cavity, and demolding the molded article in less than one minute from the time of injection, said formulation being
- A. a polyol blend comprising (parts by weight):
- ______________________________________ long chain polyol 70 to 90 [alkane diol/ triol #1 10 to 20] [alkane diol/triol #2 0.10 to 20] aromatic polyamine 3 to 4 alkylene amine catalyst 0.015 to 0.030 carbon black 0.01 to 1.0 gaseous blowing agent 3 to 8 ______________________________________
- and a crosslinker/extender blend comprising in the range of 10 to 20 parts of a first hydroxyl compound and 0.10 to 20 parts of a second hydroxyl compound different from said first hydroxyl compound, said hydroxyl compounds being selected from the group consisting of alkane diols and triols;
- with
- B. a quasi prepolymer of an alkane diol, and an MDI, said quasi prepolymer having a free NCO in the range of 22 to 24 percent;
- wherein:
- said long chain polyol has a molecular weight in the range of 3000 to 6000, a functionality in the range of 2 to 3, and an equivalent weight of 1500 to 3000;
- all of said alkane diols and triols have a molecular weight in the range of 62 to 250;
- said aromatic polyamine has the formula ##STR5##
- and n has a value in the range of 0.1 to 0.7.