Back to results
US 4,045,415 AGranted
Process for preparing copolymers of trioxane
AssigneeHoechst Aktiengesellschaft
InventorsGunter Sextro, Karlheinz Burg, Klemens Gutweiler, Klaus Durichen
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeHoechst Aktiengesellschaft
InventorsGunter Sextro, Karlheinz Burg, Klemens Gutweiler, Klaus Durichen
Estimating the term…
Copolymers of trioxane with cyclic acetals may be prepared by copolymerization of the monomers in solid phase. For this purpose the monomers are first mixed homogeneously in a liquid phase with a catalyst, the mixture is then solidified by cooling and finally polymerized by heating, while maintaining it in a solid phase. The liquid phase mixture is cooled to solidify it immediately after mixing and prior to development of turbidity in the liquid mixture. Cooling can be effected, for example, on a chilled rotating roll. The moulding composition, obtained after having worked up the copolymer as usual, is a suitable material for the preparation of molded semi-finished products and finished articles.
In a process for producing copolymers of trioxane by copolymerization of 99.9 to 90 weight percent of trioxane and 0.1 to 10 weight percent of a cyclic acetal, which process includes the steps of mixing said trioxane and cyclic acetal with a cationically active catalyst at a temperature of 62.degree. to 115.degree. C., solidifying the resulting mixture by chilling it and thereafter heating the resulting mixture to about 62.degree. to 130.degree. C. while it is maintained in a solid state to substantially complete said polymerization, the improvement which consists in chilling the liquid mixture of trioxane and acetal immediately after it is mixed and prior to the development of turbidity therein.
In a process for producing copolymers of trioxane by copolymerization of 99.9 to 90 weight percent of trioxane and 0.1 to 10 weight percent of cyclic acetal, which process includes the steps of mixing said trioxane and cyclic acetal with a cationically active catalyst at a temperature of 62.degree. to 115.degree. C., solidifying the resulting mixture by chilling it and thereafter heating the resulting mixture to about 62.degree. to 130.degree. C. while it is maintained in a solid state to substantially complete said polymerization, the improvement which consists in applying the liquid mixture to a refrigerated roll to solidify it immediately after mixing and prior to the development of turbidity therein.
A process for producing a trioxane copolymer which comprises preparing a homogeneous mixture of 99.9 to 90 weight % of trioxane, 0.1 to 10 weight % of a cyclic acetal and a cationically active catalyst at a temperature of 62.degree. to 115.degree. C., chilling the liquid mixture immediately after it is mixed and prior to the development of turbidity therein to a temperature of 40.degree. to -20.degree. C. to solidify it, polymerizing the solidified mixture at a temperature of 62.degree. to 130.degree. C. without melting and submitting the resulting copolymer to a thermal or hydrolytic controlled partial degradation down to primary alcohol terminals.
Dependencies are inferred from the claim text.