Sulfuric acid leaching of nickeliferous laterite
AssigneeAmax Inc.
InventorsPaul B. Queneau, Eddie C. Chou
Life of this patent
Estimating the term…
Abstract
The leaching efficiency of nickeliferous lateritic ore is optimized by scalping the ore to remove a coarse low-nickel fraction and provide a fine nickel-rich fraction which is then high pressure leached in a sulfuric acid solution by controlling the parameters temperature, pulp density, the rate of acid addition, leaching time, agitation rate, etc., whereby a pregnant solution is obtained with the nickel to (Fe+Al+Cr) ratio exceeding about 2.
Claims11
A process for improving the leaching efficiency of nickeliferous lateritic ore of minus 100 mesh size and containing at least about 1% by weight of nickel which comprises,
- providing in an autoclave an aqueous slurry of said ore at a pulp density of not exceeding about 33% solids,
- subjecting said slurry to high pressure leaching in a sulfuric acid solution in said autoclave at a temperature of over 260.degree. C and ranging up to about 290.degree. C at a pressure of about 700 psig to 1000 psig at an agitation rate sufficient to suspend solids in said slurry,
- the amount of sulfuric acid being injected in said autoclave in a single addition and corresponding to an acid-to-ore ratio ranging from about 0.2 to 0.35, the leaching time being sufficient to leach at least about 95% of said nickel,
- and then discharging the leached slurry into a flash tank such that the slurry is subjected to turbulence due to the release of autoclave pressure during flashdown, the slurry being then neutralized during said turbulence to a pH of at least about 1.8 but not exceeding about 4.5 to precipitate iron and aluminum and thereby inhibit dissolution of precipitated iron and aluminum downstream of said process and provide a pregnant solution having a nickel to Fe+Al+Cr ratio exceeding 2.
A process of improving the leaching efficiency of nickeliferous lateritic ore which comprises,
- providing said ore in particulate form,
- determining the particle size distribution of said ore in terms of size fractions including the nickel assay of said fractions,
- separating the coarse fractions in which the combined average nickel content by weight is less than about 0.7% nickel from fines in which the combined average nickel content by weight of said fines is at least about 1%, said separated fines fraction being less than 100 mesh in size and containing at least about 70% of the total nickel in the ore,
- providing in an autoclave an aqueous slurry of said nickel-rich fraction at a pulp density of about 20% to 30%,
- subjecting said slurry to high pressure leaching in a sulfuric acid solution in said autoclave at a temperature of over 260.degree. C and ranging up to about 290.degree. C at a pressure of about 700 psig to 1000 psig at an agitation rate sufficient to suspend solids in said slurry,
- the amount of acid being injected in said autoclave in a single addition and corresponding by weight to an acid-to-ore ratio of about 0.2:1 to 0.35:1,
- discharging said leached slurry into a flask tank such that said slurry is subjected to turbulence due to the release of autoclave pressure during flashdown,
- and neutralizing said leached slurry to a pH of at least about 1.8 but not exceeding about 4.5 to precipitate iron and aluminum while under said state of turbulence and inhibit dissolution of precipitated iron and aluminum downstream of said process,
- thereby leaching at least about 95% of the nickel and provide a pregnant liquor in which the nickel to (Fe+Al+Cr) ratio exceeds about 2.