Abstract
The polyolefin containing emulsion adhesives of the present invention comprise an aqueous emulsion of a blend comprising an oxidized polyethylene, a tackifying resin and emulsifiers. The emulsion adhesives have a novel combination of properties including a long shelf life, are not adversely affected by freezing, and provide adhesive bonds having good shear strength and relatively low tensile strength.
Claims6
An adhesive composition comprising an emulsion of (1) 5 to 35 weight percent oxidized polyethylene having a melt viscosity in the range of about 200 cp. to about 1500 cp., an inherent viscosity of about 0.05 to 0.5 and an acid number of about 4 to 30, (2) 10 to 50 weight percent of at least one tackifying resin selected from the group consisting of hydrocarbon resins and polyterpene resins (3) 5 to 25 weight percent emulsifiers and (4) 5 to 80 weight percent water.
An adhesive composition comprising an emulsion of (1) 10 to 25 weight percent oxidized polyethylene having a melt viscosity in the range of about 200 cp. to about 1500 cp., an inherent viscosity of about 0.05 to 0.5 and an acid number of about 4 to 30, (2) 15 to 35 weight percent of at least one tackifying resin selected from the group consisting of hydrocarbon resins and polyterpene resins, (3) 10 to 25 weight percent emulsifiers, and (4) 20 to 65 weight percent water.
An adhesive composition comprising an emulsion of (1) 5 to 35 weight percent oxidized polyethylene having a melt viscosity in the range of about 200 cp. to about 1500 cp., an inherent viscosity of about 0.05 to 0.5 and an acid number of about 12 to 17, (2) 10 to 50 weight percent of a tackifying resin comprising at least one hydrocarbon resin having a softening point of about 100.degree. C., (3) 5 to 25 weight percent emulsifiers and (4) 5 to 80 weight percent water.
An adhesive composition comprising an emulsion of (1) 5 to 35 weight percent oxidized polyethylene having a melt viscosity in the range of about 200 cp. to about 1500 cp., an inherent viscosity of about 0.05 to 0.5 and an acid number of about 12 to 17, (2) 10 to 50 weight percent of a tackifying resin comprising a mixture of hydrocarbon resins, (3) 5 to 25 weight percent emulsifiers and (4) 5 to 80 weight percent water.
An adhesive composition comprising an emulsion of (1) 10 to 25 weight percent oxidized polyethylene having a melt viscosity in the range of about 200 cp. to about 1500 cp., an inherent viscosity of about 0.05 to 0.5 and an acid number of about 12 to 17, (2) 15 to 35 weight percent of a tackifying resin comprising at least one hydrocarbon resin having a softening point of about 100.degree. C., (3) 10 to 25 weight percent emulsifiers and (4) 20 to 65 weight percent water.
An adhesive composition comprising an emulsion of (1) 10 to 25 weight percent oxidized polyethylene having a melt viscosity in the range of about 200 cp. to about 1500 cp., an inherent viscosity of about 0.05 to 0.5 and an acid number of about 12 to 17, (2) 15 to 35 weight percent of a tackifying resin comprising a mixture of hydrocarbon resins, (3) 10 to 25 weight percent emulsifiers and (4) 20 to 65 weight percent water.
Dependencies are inferred from the claim text.