Surgical implant and alloy for use in making an implant
AssigneeInstitut Dr. Ing. Reinhard Straumann AG
InventorsSamuel G. Steinemann, Stephan M. Perren
Life of this patent
Estimating the term…
Abstract
Implant for bone surgery and for dental therapeutics, comprising an alloy containing defined critical amounts of titanium and/or zirconium, and other selected elements including niobium, tantalum, chromium, molybdenum and aluminum. Dissolved gases may also be included. The alloy is free from copper, cobalt, nickel, vanadium and tin, apart from the usual impurities.
Claims18
Implant for bone, joint or dental surgery consisting essentially of a worked and heat-treated alloy composition having full tissue compatibility and a tensile strength of not less than about 100 kg/mm.sup.2 and fatigue strength of at least about 40 kg/mm.sup.2, said alloy composition consisting essentially of:
- i. a first component constituting about 3% to about 30% by weight of said alloy composition, said first component consisting essentially of not less than one member selected from the group consisting of niobium, tantalum, chromium, molybdenum, aluminum;
- and the balance
- ii. a second component of said alloy composition consisting essentially of not less than one member selected from the group consisting of titanium and zirconium;
- wherein the sum of the weights of chromium, molybdenum, and aluminum in said alloy composition amounts to at least 20% by weight of said alloy composition, and the weight of zirconium therein amounts to not more than 75% by weight of said alloy composition;
- said alloy composition being free from copper, cobalt, nickel, vanadium and tin, apart from the usual impurities.
Method of using a durable, workable, non-toxic alloy as an implant for bone, joint or dental surgery which comprises providing an implant of a worked and heat-treated alloy composition consisting essentially of
- i. a first component constituting from about 3% to about 30% by weight of said alloy composition and consisting essentially of not less than one member selected from the group consisting of niobium, tantalum, chromium, molybdenum, and aluminum;
- and the balance
- ii. a second component consisting of not less than one member selected from the group consisting of titanium, and zirconium
- wherein the sum of the weights of chromium, molybdenum, and aluminum in said alloy composition amounts to not more than 20% by weight of said alloy composition, and the weight of zirconium in said alloy composition amounts to not more than 75% by weight of said alloy composition;
- said alloy composition being free from copper, cobalt, nickel, vanadium, and tin, apart from the usual impurities, said alloy composition having a tensile strength of at least about 100 kg/mm.sup.2 and fatigue strength of at least about 40 kg/mm.sup.2, and positioning said implant in a living subject undergoing bone joint or dental surgery for internal fixation or repair of a fractured bone, joint or tooth.
Method of making an implant for bone, joint or dental surgery, which comprises:
- a. providing a worked and heat-treated alloy composition having full tissue compatibility, said alloy composition consisting essentially of:
- i. a first component of said alloy composition constituting about 3% to about 30% by weight thereof, and consisting essentially of not less than one member selected from the group consisting of niobium, tantalum, chromium, molybdenum, and aluminum;
- and the balance
- ii. a second component of said alloy composition consisting essentially of not less than one member selected from the group consisting of titanium, and zirconium,
- wherein the sum of the weights of chromium, molybdenum and aluminum in said alloy composition about to not more than 20% by weight of said alloy, and the weight of zirconium therein amounts to at most 75% by weight of said alloy composition;
- said alloy composition being free from copper, cobalt, nickel, vanadium and tin, apart from the usual impurities;
- b. shaping the alloy composition to the desired form of implant;
- and
- c. subjecting the so-shaped alloy composition to heat treatment, whereby an implant is obtained composed of alloy having a tensile strength at least about 100 kg/mm.sup.2 and fatigue strength of at least about 40 kg/mm.sup.2.