Abstract
Hexagonal plate crystals of aluminum sulfate are produced in chemically pure form by a process which comprises cooling a heated saturated solution of chemically impure aluminum sulfate acidified with sulfuric acid to precipitate crystals of aluminum sulfate, heating the slurry of the cooled solution containing the precipitated aluminum sulfate crystals to a predetermined temperature wherein the temperature is maintained for a time sufficient to dissolve a portion of the crystals in the solution, cooling the heated slurry to precipitate aluminum sulfate crystals, and separating the precipitated crystals from the slurry.
Claims4
A process for the production of hexagonal plate crystals of aluminum sulfate, which comprises the steps of:
- a. cooling at a rate of less than 8.degree. C./hour a hot, chemically impure saturated solution of aluminum sulfate acidified with sulfuric acid which contains 50-85 g/l of Al.sub.2 O.sub.3 and the weight ratio of SO.sub.3 to Al.sub.2 O.sub.3 in the saturated solution is in the range of 4:1 to 10:1 to precipitate crystals of aluminum sulfate, the solution containing iron sulfate in an amount such that the iron sulfate is not precipitated with the aluminum sulfate crystals;
- b. heating the resultant slurry containing the precipitated aluminum sulfate crystals to a temperature below the minimum temperature at which all the precipitated aluminum sulfate is capable of dissolving in the solution and maintaining it at that temperature for at least one hour to dissolve only a part of the crystals in the solution;
- c. cooling the slurry to cause the aluminum sulfate crystals to grow;
- and
- d. recovering said hexagonal plate aluminum sulfate crystals from the slurry
A process for the production of hexagonal plate crystals of chemically pure aluminum sulfate which comprises:
- a. cooling at a rate of less than 8.degree. C./hour a hot, chemically impure saturated solution of aluminum sulfate, acidified with sulfuric acid, which contains 50-85 g/l of Al.sub.2 O.sub.3, wherein the weight ratio of SO.sub.3 to Al.sub.2 O.sub.3 in the saturated solution is in the range of 4:1 to 10:1 to precipitate crystals of aluminum sulfate, and wherein said solution contains iron sulfate in an amount such that the iron sulfate is not precipitated with the aluminum;
- b. heating the resultant slurry containing the precipitated aluminum sulfate crystals to a temperature below the minimum temperature at which all the precipitated aluminum sulfate will dissolve into the solution, and maintaining said slurry at said temperature for at least one hour to dissolve only a portion of the crystals in the solution;
- c. cooling the slurry to cause the aluminum sulfate crystals to grow;
- d. recovering hexagonal plate aluminum sulfate crystals to be used as seed crystals for subsequent processing;
- adding 5% of said seed crystals to additional amounts of said hot impure saturated solution of aluminum sulfate to form a slurry;
- adjusting the sulfuric acid concentration in said slurry to from 43-50 wt.%;
- heating the slurry to a temperature at which essentially pure hexagonal plate aluminum sulfate crystals begin to grow;
- maintaining the slurry at this temperature for less than three hours;
- cooling said slurry at a rate not exceeding less than 8.degree. C./hour to cause said hexagonal plate aluminum sulfate crystals to grow;
- and
- recovering hexagonal plate aluminum sulfate crystals.