Cellular isocyanurate polymer
AssigneeThe Upjohn Company
InventorsRichard A. Kolakowski, Harold E. Reymore, Jr., Adnan A. R. Sayigh
Life of this patent
Estimating the term…
Abstract
Polyisocyanurate foams are disclosed which are characterized by low Flame Spread Ratings and low smoke generation values, as determined by the Underwriter's Laboratory Tunnel Test in accordance with the ASTM E-84 test procedure. The smoke and flame resistant properties are achieved, not through the use of flame retardants or additives, but rather by the use of a minor amount of a hydroxyl terminated aromatic polyester having a hydroxyl equivalent weight from about 150 to about 500 and which is the product of the reaction of an excess of a polyethyleneglycol having an equivalent weight from about 75 to about 225, with an aromatic polycarboxylic compound.
Claims11
In a polymer in which the major recurring polymer unit is isocyanurate which polymer comprises the reaction product obtained by bringing together a polymethylene poly(phenylisocyanate), a trimerization catalyst and a minor amount of a polyol the improvement which comprises employing as the polyol component from about 0.05 hydroxyl equivalent to about 0.20 hydroxyl equivalent per equivalent of said polymethylene poly(phenylisocyanate) of a polyol having a hydroxyl equivalent weight from about 150 to about 500 provided the polyol is present in a weight from about 10 to about 30 parts per equivalent of said isocyanate, and said polyol is obtained by the reaction of:
- a. about 0.1 molar to about 0.7 molar excess of a polyethyleneglycol having a hydroxyl equivalent weight from about 75 to about 225 over the stoichiometric amount required for reaction with b. an aromatic polycarboxylic compound containing from two to three carboxylic groups.
In a cellular polymer in which the major recurring polymer unit is isocyanurate which polymer comprises the reaction product obtained by bringing together in the presence of a blowing agent, a polymethylene poly(phenylisocyanate), a trimerization catalyst and a minor amount of a polyol the improvement which comprises employing as the polyol component from about 0.05 hydroxyl equivalent to about 0.20 hydroxyl equivalent per equivalent of said polymethylene poly(phenylisocyanate) of a polyol having a hydroxyl equivalent weight from about 150 to about 500 provided the polyol is present in a weight from about 10 to about 30 parts per equivalent of said isocyanate and said polyol is obtained by the reaction of:
- a. about 0.1 molar to about 0.7 molar excess of a polyethyleneglycol having a hydroxyl equivalent weight from about 75 to about 225 over the stoichiometric amount required for reaction with
- b. an aromatic polycarboxylic compound containing from two to three carboxylic groups.
A cellular polymer in which the major recurring polymer unit is isocyanurate which polymer comprises the reaction product obtained by bringing together in the presence of a blowing agent:
- A. a polymethylene poly(phenylisocyanate) which contains from about 35 percent to about 85 percent by weight of methylenebis(phenylisocyanate), the balance of said isocyanate having a functionality higher than 2;
- B. a catalytic amount of a trimerization catalyst comprising the combination of:
- i. a glycidyl ether of a novolac resin having a functionality of at least two;
- ii. N,N-dimethylcyclohexylamine;
- and
- iii. sodium N-(2-hydroxy-5-nonylphenyl)methyl-N-methyl glycinate;
- and
- C. from about 0.05 hydroxyl equivalent to about 0.20 hydroxyl equivalent per equivalent of said polymethylene poly(phenylisocyanate) of a polyol having a hydroxyl equivalent weight from about 150 to about 500 provided the polyol is present in a weight from about 10 to about 30 parts per equivalent of said isocyanate and said polyol is obtained by the reaction of:
- a. about 0.1 molar to about 0.7 molar excess of a polyethyleneglycol having a hydroxyl equivalent weight from about 75 to about 225 over the stoichiometric amount required for reaction with
- b. trimellitic anhydride.
A cellular polymer in which the major recurring polymer unit is isocyanurate which polymer comprises the reaction product obtained by bringing together in the presence of a blowing agent:
- A. a polymethylene poly(phenylisocyanate) which contains from about 45 percent by weight to about 50 percent by weight of methylenebis(phenylisocyanate) and the balance of said isocyanate having a functionality higher than 2, and said polymethylene poly(phenylisocyanate) further characterized by having a % hot HCl acidity of less than 0.1%;
- B. a catalytic amount of a trimerization catalyst comprising the combination of:
- i. a glycidyl ether of a novolac resin having a functionality of at least two;
- ii. N,N-dimethylcyclohexylamine;
- and
- iii. sodium N-(2-hydroxy-5-nonylphenyl)methyl-N-methyl glycinate;
- and
- C. from about 0.05 hydroxyl equivalent to about 0.20 hydroxyl equivalent per equivalent of said polymethylene poly(phenylisocyanate) of a polyol having a hydroxyl equivalent weight from about 200 to about 300 provided the polyol is present in a weight from about 10 to about 30 parts per equivalent of said isocyanate and said polyol is obtained by the reaction of from about 3.2 to about 3.6 moles of tetraethyleneglycol with 1 mole of trimellitic anhydride.
Dependencies are inferred from the claim text.