Shaped articles of hydraulic cement compositions having a reflective surface
OwnerMark Plunguian, Charles E. Cornwellinventors
Life of this patent
Estimating the term…
Abstract
Shaped articles such as tiles and panels are produced from aqueous slurries of hydraulic cement, with or without aggregate, to which "super" water reducers have been admixed, by casting in a synthetic polymer mold with glossy, water-repellent surface, to yield castings with highly reflective, glassy surfaces. Color pigments may be added to the formulation to yield castings with reflective, glossy colored surfaces.
Claims4
A method of producing a shaped article with a glossy surface comprising the steps of dispersing in water about 100 parts by weight of a hydraulic cement, selected from the group consisting of portland cement, and gypsum cement;
- 10-400 parts aggregate;
- 0.25-2.0 parts of a cement dispersing agent selected from the group of polymers consisting of the alkali metal salts of melamine sulfonic acid partially condensed with formaldehyde, the alkali metal salt of naphthalene sulfonic acid partially condensed with formaldehyde, and about 30-90 percent of the alkali metal salt of a high molecular weight condensation product of naphthalene-sulfonic acid and the balance 70-10 percent being the alkali metal salt of gluconic acid;
- 0.01-0.1 parts of a cement curing retarder;
- and 0-10 parts color pigment, all in parts by weight;
- using the dispersion thus formed to fill a synthetic polymer mold having a glossy, water-repellent surface, or a mold coated with a synthetic polymer, said polymer being selected from the group consisting of polystyrene, polypropylene, and polyacrylic resins;
- filling the mold with the cementitious composition, curing the casting, and then removing it from the mold.