Catalytic cracking process using ammonia-stable zeolite catalyst
AssigneeUnion Oil Company of America
InventorJohn W. Ward
Life of this patent
Estimating the term…
Abstract
Highly active, hydrothermally stable and ammonia-stable Y zeolite compositions are disclosed, which compositions are useful as adsorbents, hydrocarbon conversion catalysts, and as acidic supports for catalytic metals. The stabilized Y zeolite composition is prepared from a sodium Y zeolite by a novel sequence of: (1) partial exchange of ammonium ions for sodium ions, (2) steam calcination under controlled conditions of time, temperature and steam partial pressure, and (3) further ion exchange of ammonium ions for sodium ions to reduce the final Na.sub.2 O content to below about one weight-percent.
Claims10
A process for the catalytic cracking of a hydrocarbon feedstock to produce lower boiling hydrocarbons, which comprises contacting said feedstock, under non-hydrogenative cracking conditions, with a cracking catalyst comprising a major proportion of a refractory oxide of a difficulty reducible metal, and intimately admixed therewith a minor proportion of an ammonia-stable Y zeolite composition prepared by the steps of:
- 1. calcining an ammonium-sodium Y zeolite containing about 0.6 - 5 weight-percent of sodium as Na.sub.2 O, said calcining being carried out at a temperature between about 600.degree. and 1650.degree. F. in contact with at last about 0.2 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.40 and 24.64 A;
- 2. subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 25 percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 1 weight-percent Na.sub.2 O;
- and
- 3. calcining the product from step (2) at a temperature between about 600.degree. and 1500.degree. F. for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size thereof to below about 24.40 A.
A process for the catalytic cracking of a gas oil feedstock to produce gasoline boiling range hydrocarbons, which comprises contacting said feedstock, under non-hydrogenative cracking conditions, with a cracking catalyst comprising a major proportion of a refractory oxide of a difficulty reducible metal, and intimately admixed therewith a minor proportion of an ammonia-stable Y zeolite composition prepared by the steps of:
- 1. calcining an ammonium-sodium Y zeolite containing about 1 - 4 weight-percent of sodium as Na.sub.2 O, said calcining being carried out at a temperature between about 800.degree. and 1650.degree. F. in contact with between about 2-15 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.42 and 24.62 A;
- 2. subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 70 percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 0.6 weight-percent Na.sub.2 O;
- and
- 3. calcining the product from step (2) at a temperature between about 800.degree. and 1500.degree. F. for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size thereof to below about 24.40 A.