Preparation of cellulose nitrite
OwnerRichard G. Schweigerinventor
Life of this patent
Estimating the term…
Abstract
Preparation of partially substituted nitrate and sulfate esters of polysaccharides or polyvinylalcohol, their esters containing a mixture of nitrite with sulfate or nitrate groups, aqueous media thickened with such esters, the simultaneous preparation of such esters and alkyl nitrites or such esters and inorganic nitrites or nitrates and resulting products, useful as thickeners, films, fibers and in many other applications.
Claims10
A process for preparing a nitrite ester of cellulose, said process comprising:
- reacting cellulose which contains from aout 4 to about 12 percent by weight of water with dinitrogentetroxide or nitrosyl chloride in the presence of a swelling or solubilizing solvent for the resulting cellulose nitrite and a proton acceptor;
- said water being substantially uniformly distributed throughout the cellulose reactant;
- said reaction being carried out at a reaction temperature below about 50.degree. C., and
- said solvent being present in an amount sufficient to provide at least about three parts by weight of solvent for each part of cellulose.
A process for preparing a nitrite ester of cellulose, said process comprising:
- treating cellulose which contains in excess of about 4 percent by weight of water distributed substantially uniformly throughout the cellulose with a highly polar aprotic solvent to reduce the water content in said cellulose to less than about 4 percent by weight of the cellulose;
- reacting the treated cellulose with dinitrogentetroxide or nitrosyl chloride in the presence of a swelling or solubilizing reaction solvent for the cellulose nitrite ester and a proton acceptor;
- said reaction being carried out at a reaction temperature below about 50.degree. C., and
- said reaction solvent being present in an amount sufficient to provide at least about three parts by weight of solvent for each part of cellulose.
A nitrite ester of cellulose having a degree of substitution of less than about 2.0.