Abstract

The method of treating a textile fabric comprising cellulosic fibers to produce a modified fabric intermediate from which permanently shaped wearing apparel having an improved dry crease recovery can be made, comprising the steps of: (1) impregnating the material with a cellulose cross-linking reagent selected from the groups consisting of: (a) reaction products of formaldehyde with carboxamides wherein said reaction products contain 2 or 3 N-methylol groups and methyl ethers thereof; (b) compounds having the following generic formula: R.sub.1 OCH.sub.2 CH.sub.2 SO.sub.2 (QSO.sub.2).sub.n CH.sub.2 CH.sub.2 OR.sub.2 where R.sub.1 and R.sub.2 are selected from the group consisting of hydrogen and an alkyl radical of up to five carbon atoms; Q is a divalent organic radical selected from the group consisting of aliphatic radicals containing at least three carbon atoms, aromatic radicals and aklylaromatic radicals; and n is 0 or 1, and said reaction conditions include the presence of an alkaline catalyst; (c) compounds have the following generic formula: ##STR1## where R.sub.1, R.sub.2, and R.sub.3 are selected from the group consisting of hydrogen and alkyl radicals having up to five carbon atoms; Q is a divalent organic radical; W is an electronegative activating group such as --CO--, --CONH, and the like; and n has a value of 0 or 1; and (d) compounds having 2 or 3 N-hydroxypropyl groups and methyl ethers thereof; (2) heating the impregnated fabric in an atmosphere in which the relative humidity is less than 100% in the presence of a catalyst to a temperature for a time sufficient to chemically bond the cross-linking reagent to the cellulosic fibers, thereby producing the modified fabric intermediate in which the reacted cross-linking reagent is insolubilized to the extent that the reacted reagent would not be removed by washing the fabric, the modified fabric intermediate having a dry crease recovery angle which is increased by at least 10% by subsequently heating the fabric.

Claims20

Dependent claims

The method of producing a permanently shaped textile article from a material comprising cellulosic fibers comprising the steps of:

A. shaping a material into a desired configuration, said material comprising cellulosic fibers and which material has been:
(1) impregnated with a cellulose cross-linking reagent selected from the group consisting of:
(a) reaction products of formaldehyde with carboxamides wherein said reaction products contain 2 or 3 N-methylol groups and methyl ethers thereof;
(b) compounds having the following generic formula:
R.sub.1 OCH.sub.2 CH.sub.2 SO.sub.2 (QSO.sub.2).sub.n CH.sub.2 CH.sub.2 OR.sub.2
wherein R.sub.1 and R.sub.2 may be the same or different and are selected from the group consisting of hydrogen and an alkyl radical of up to five carbon atoms;
Q is a divalent organic radical selected from the group consisting of aliphatic radicals containing at least three carbon atoms, aromatic radicals and alkylaromatic radicals;
and, n is 0 or 1;
and, said reaction conditions include the presence of an alkaline catalyst;
(c) compounds selected from the group consisting of 1,3,5 tris (hydroxypropyl) hexahydro-s-triazine and 1,3,5 tris (methoxypropyl) hexahydro-s-triazine and,
(d) tris-1-aziridinyl phosphine oxide;
and,
(2) heated in an atmosphere in which the relative humidity is less than 100% and in the presence of a catalyst, to a temperature in the range of between about 200.degree. F. to about 1000.degree. F. for a period of time in the range of between about 5 minutes and about 4 seconds during which time period said cross-linking reagent is chemically bonded to said cellulosic material, said time-temperature relationship being such that in the lower temperature range the time period is in the higher time range and in the higher temperature range the time period in the lower time range and under such heating conditions that the maximum heat energy applied to said impregnated material is that heat energy which allows said material to have a maximum dry crease recovery angle increasable by at least 10% by subsequent heating to cure said material, to thereby produce a modified material intermediate;
and
B. without further addition of catalysts to said material, heating the shaped material to cure said chemically bonded cross-linking reagent to provide a permanently shaped textile article having at least said increased dry crease recovery angle.

12 more elements

The method of producing a permanently shaped wearing garment having an improved dry crease recovery angle from a textile fabric comprising cellulosic fibers comprising the steps of:

(1) impregnating a fabric comprising cellulosic fibers with a cellulose cross-linking reagent selected from the group consisting of:
(a) reaction products of formaldehyde with carboxamides wherein said reaction products contain (2) or 3 N-methylol groups and methyl ethers thereof;
(b) compounds having the following generic formula:
R.sub.1 OCH.sub.2 CH.sub.2 SO.sub.2 (QSO.sub.2).sub.n CH.sub.2 CH.sub.2 OR.sub.2
wherein R.sub.1 and R.sub.2 may be the same or different and are selected from the group consisting of hydrogen and an alkyl radical of up to five carbon atoms;
Q is a divalent organic radical selected from the group consisting of aliphatic radicals containing at least three carbon atoms, aromatic radicals and alkylaromatic radicals;
and, n is 0 or 1;
and, said reaction conditions include the presence of an alkaline catalyst;
(c) compounds selected from the group consisting of 1,3,5 tris (hydroxypropyl) hexahydro-s-triazine and 1,3,5 tris (methoxypropyl) hexahydro-s-triazine;
and,
d. tris-1-aziridinyl phosphine oxide;
and,
(2) heating said impregnated fabric in an atmosphere in which the relative humidity is less than 100% and in the presence of a catalyst, to a temperature in the range of between about 200.degree. F. to about 1000.degree. F. for a period of time in the range of between about 5 minutes and about 4 seconds during which time period said cross-linking reagent is chemically bonded to said cellulosic material, said time-temperature relationship being such that in the lower temperature range the time period is in the higher time range and in the higher temperature range the time period is in the lower time range and under such heating conditions that the maximum heat energy applied to said impregnated fabric is that heat energy which allows said fabric to have a maximum dry crease recovery angle increasable by at least 10% by subsequent heating to cure said material, thereby producing a modified fabric intermediate;
and without further addition of catalyst to said fabric,
(3) shaping the fabric to a desired garment configuration;
and,
(4) heating the shaped fabric to cure said chemically bonded cross-linking reagent to provide a permanently shaped garment having at least said increased dry crease recovery angle.

14 more elements

The method of producing a permanently shaped textile article from a material comprising cellulosic fibers comprising the steps of:

A. shaping a material into a desired configuration, said material comprising cellulosic fibers and which material has been:
(1) impregnated with a cellulose cross-linking reagent selected from the group consisting of:
(a) reaction products of formaldehyde with carboxamides wherein said reaction products contain 2 or 3 N-methylol groups and methyl esters thereof;
(b) compounds having the following generic formula:
R.sub.1 OCH.sub.2 CH.sub.2 SO.sub.2 (QSO.sub.2).sub.n CH.sub.2 CH.sub.2 OR.sub.2
wherein R.sub.1 and R.sub.2 may be the same or different and are selected from the group consisting of hydrogen and an alkyl radical of up to five carbon atoms;
Q is a divalent organic radical selected from the group consisting of aliphatic radicals containing at least three carbon atoms, aromatic radicals and alkylaromatic radicals;
and, n is 0 or 1;
and, said reaction conditions include the presence of an alkaline catalyst;
(c) compounds selected from the group consisting of 1,3,5 tris (hydroxypropyl) hexahydro-s-triazine and 1,3,5 tris (methoxypropyl) hexahydro-s-triazine;
and
(d) tris-1-aziridinyl phosphine oxide;
and,
(2) heated in an atmosphere in which the relative humidity is less than 100% and in the presence of a catalyst, to a temperature in the range of between about 200.degree. F. to about 1000.degree. F. for a period of time in the range of between about 5 minutes and about 4 seconds during which time period said cross-linking reagent is chemically bonded to said cellulosic material, said time-temperature relationship being such that in the lower temperature range the time period is in the higher time range and in the higher temperature range the time period is in the lower time range and under such heating conditions that the maximum heat energy applied to said impregnated material is that heat energy which allows said material to have a maximum dry crease recovery angle increasable by at least 10% by subsequent heating to cure said material, to thereby produce a modified material intermediate;
and,
(3) washed to remove the unreacted cross-linking reagent and impregnated with a catalyst suitable for catalyzing the cross-linking of said cellulose cross-linking reagent;
and,
B. heating the shaped material to cure said chemically bonded cross-linking reagent to provide a permanently shaped textile article having at least said increased dry crease recovery angle.

15 more elements

Dependencies are inferred from the claim text.

Controlling degree of reaction by controlling heat input in cellulose textile-reactant systems

Life of this patent

Controlling degree of reaction by controlling heat input in cellulose textile-reactant systems

Life of this patent

Abstract

Claims20