US 4,032,327 AGranted

Pyrometallurgical recovery of copper from slag material

AssigneeKennecott Copper Corporation

InventorsJohn W. Donaldson, Sheree N. Sharma, Nicholas John Themelis

Life of this patent

Estimating the term…

Loading patent…

Abstract

A cyclic, two-stage process is disclosed for pyrometallurgical recovery of copper as a high-grade matte from molten slag material containing both dissolved and/or entrained copper values. A charge of the copper-bearing slag material is treated in the first stage of the process with a hydrocarbonaceous or hydrogenous reductant in a rotary furnace, such as a top-blown rotary reactor, rotating at at least about 10 rpm, to form a high-grade copper matte phase and a slag phase of reduced copper content. The rotation of the reactor is discontinued and the high-grade copper matte phase separates from the slag phase and is recovered from the reactor. The reactor containing the remaining slag of reduced copper content is again rotated at about 10 rpm, and iron sulfide, e.g. pyrite, is added in the second stage of the process to the slag in the rotating reactor to provide a low-grade matte phase which literally "washes out" most of the remaining copper contained in the slag. The rotation of the reactor is again discontinued and the low-grade matte phase separates from the remaining slag phase. The remaining slag phase is removed from the reactor, and the low-grade matte produced in the second stage is left in the reactor to mix with an additional charge of slag material in a subsequent cycle of the process.

Claims6

Dependent claims

A cyclic, two-stage process for recovering essentially all copper values present in molten slag, comprising:

(a) subjecting a charge of the molten slag to vigorous agitation in a rotary reactor rotating at a speed of at least about 10 rpm;
(b) adding a carbonaceous or hydrogenous reductant to said charge of molten slag in the rotating reactor to reduce magnetite and to produce a high-grade matte, containing at least about 70% copper, and a slag;
(c) discontinuing rotation of the reactor, thereby allowing the high-grade matte to separate from the slag, whereby a matte phase and a slag phase are produced from the original charge;
(d) recovering the high-grade matte phase from the reactor;
(e) subjecting the molten slag phase that remains after the high-grade matte phase has been separated therefrom to vigorous agitation by again rotating the reactor at a speed of at least about 10 rpm;
(f) adding an iron sulfide to the molten slag in the reactor, to provide a low-grade copper matte containing from about 20% to about 35% copper and a slag containing from about 0.3% to 0.5% copper, said low-grade matte and slag being intimately mixed by vigorous agitation as the reactor rotates, thereby extracting copper values from the slag;
(g) again discontinuing rotation of the reactor, thereby allowing the low-grade copper matte to settle and to separate from the slag, whereby a matte phase are produced from the slag phase of step (c);
(h) removing the slag phase of step (g) from the reactor, leaving the low-grade copper matte phase in the reactor;
(i) introducing an additional charge of the molten slag into the reactor for mixing with the low-grade copper matte remaining therein from step (h);
and repeating steps (a) through (i) on a cyclic basis.

7 more elements

Dependencies are inferred from the claim text.