Coated fabrics and laminated articles therefrom
AssigneeE. I. Du Pont de Nemours and Company
InventorEdward Lung Yuan
Life of this patent
Estimating the term…
Abstract
A coated triaxial fabric, a process for its preparation and a laminated article prepared therefrom are provided. The coated fabric comprises a triaxial fabric, such as glass or polyester fibers, having a polymeric material impregnating and coating the fabric in an amount sufficient to set the yarn courses of the fabric where they cross one another and to give such a coated fabric superior isotropic tear resistance and strength (substantially uniform in all directions) when compared to a similarly constructed coated fabric prepared from a conventional biaxial fabric or a conventional bias ply construction. The coated fabric can be bonded to substrates such as metals and polymeric films.
Claims10
A coated article comprising:
- a triaxial woven fabric and a polymeric material impregnating and coating said fabric, said polymeric material present in an amount sufficient to set the yarn courses of said fabric where they cross one another and so that said coated fabric has:
- a. a tensile strength, measured at the weakest direction according to ASTM D-1682-64, of at least three times the uncoated fabric;
- b. a tensile strength, measured at the weakest direction according to ASTM D-1682-64, of at least 50% of that measured in the transverse direction;
- and
- c. an average tongue tear resistance of the machine and transverse directions measured according to ASTM D-2261-64 of at least twice the tensile strength of an individual yarn used in the woven fabric
- wherein the triaxial woven fabric is of fibers selected from the group consisting of glass, polyester, cotton, polyamide and aromatic polyamide and blends thereof;
- wherein the polymeric material is selected from the group consisting of an elastomer, an epoxy resin, an acrylic resin, a polyester resin and a perfluorocarbon resin;
- and
- wherein the polymeric material to fabric weight ratio is within the range of about 0.2 to 2.
A coated article comprising:
- a triaxial woven fabric of glass fibers, polyethylene terephthalate fibers or a blend of polyethylene terephthalate fibers and cotton fibers and a polymeric material impregnating and coating said fabric to a coating to fabric weight ratio within the range of about 0.2 to 2, said polymeric material impregnating the fabric so as to set the yarn courses where they cross one another and selected from the group consisting of an acrylic resin, an epoxy resin and a nitrile rubber, said coated fabric having:
- a. a tensile strength, measured at the weakest direction according to ASTM D-1682-64, of at least three times the uncoated fabric;
- b. a tensile strength, measured at the weakest direction according to ASTM D-1682-64, of at least 60% of that measured in the transverse direction;
- and
- c. an average tongue tear resistance of the machine and transverse directions measured according to ASTM D-2261-64 of at least twice the tensile strength of an individual yarn used in the woven fabric.
A process for preparing a coated article comprising:
- applying to a triaxial woven fabric a polymeric material in an amount sufficient to set the yarn courses of the fabric where they cross one another and subsequently applying a polymeric material to the fabric with the applied polymeric material to the fabric with the applied polymeric material in an amount sufficient to give a coated fabric having:
- a. a tensile strength, measured at the weakest direction according to ASTM D-1682-64, of at least three times the uncoated fabric;
- b. a tensile strength, measured at the weakest direction according to ASTM D-1682-64, of at least 50% of that measured in the transverse direction;
- and
- c. an average tongue tear resistance of the machine and transverse directions measured according to ASTM D=2261-64 of at least twice the tensile strength of an individual yarn used in the woven fabric;
- wherein the triaxial woven fabric is made of fibers selected from the group consisting of glass, polyester, cotton, polyamide and aromatic polyamide and blends thereof and the polymeric material is selected from the group consisting of an elastomer, an epoxy resin, and acrylic resin, a polyester resin and a perfluorocarbon resin.