Composition for making garnet films for improved magnetic bubble devices

A flux composition from which single crystal garnet films having growth induced uniaxial anisotropy can be epitaxially grown which comprises essentially of about 75 mol percent of lead oxide, about 15 mol percent of bismuth oxide, from about 8 - 8.5 mol percent of iron oxide, from about 0.5 - 1.0 mol percent of an oxide selected from one or more of the group consisting of yttrium oxide and trivalent rare earth oxides and from about 1 - 1.5 mol percent of gallium oxide, aluminum oxide or a mixture of gallium and aluminum oxides.