Structured-particle latexes
AssigneeThe Dow Chemical Company
InventorsDale S. Gibbs, Earl H. Wagener, Ritchie A. Wessling
Life of this patent
Estimating the term…
Abstract
Structured-particle latexes are prepared from nonionic or slightly cationic latexes, either preformed or polymerized in situ, by emulsion polymerizing monomeric materials which include an ethylenically unsaturated, activated-halogen monomer such as vinylbenzyl chloride in the absence of a sufficient amount of a surfactant to initiate new particles whereby the activated-halogen monomer is copolymerized on the surface of the existing particles which are dispersed in aqueous media. To the resulting structured particle latex may then be added conventional cationic surfactants to provide greater stability. The cationic latexes are suitable for coatings.
Claims17
An aqueous colloidal dispersion of structured particles having activated halogens at or near their surface, said particles consisting of a nonionic, organic polymer core having adhered thereto a thin layer of water-insoluble copolymer of an ethylenically unsaturated, nonionic monomer which is devoid of an activated-halogen and a nonionic emulsion polymerizable, oil-soluble, ethylenically unsaturated, activated-halogen monomer which does not inhibit free-radical polymerization, can diffuse through an aqueous medium and does not hydrolyze readily in such aqueous medium;
- said thin layer having a thickness of from a monomolecular layer to about 100 Angstroms;
- the amount of said activated-halogen monomer copolymerized in the thin layer ranging from about 0.01 milliequivalent to about 1.4 milliequivalent per gram of particles in the dispersion and not more than 3.0 milliequivalents for each gram of copolymer in the thin layer;
- said dispersion being stabilized by a small, stabilizing amount up to about 0.25 milliequivalent per gram of structured particles of a cationic surfactant or blend of cationic and nonionic surfactants.
In a latex comprising an aqueous colloidal dispersion of a nonionic, organic polymer in the form of particles having a surface on which is adsorbed a surfactant and having a particle diameter of from about 500 Angstroms to about 10,000 Angstroms, the improvement comprising particles which are structured particles having activated-halogens chemically bound to the particle at or near the surface and the surfactant being a cationic surfactant or a blend of cationic and nonionic surfactants;
- said structured particles consisting of a non-reactive, nonionic, organic polymer core encapsulated with a thin layer of a water-insoluble copolymer of an ethylenically unsaturated, nonionic monomer which is devoid of an activated-halogen and a nonionic, emulsion polymerizable, oil-soluble ethylenically unsaturated, activated-halogen monomer which does not inhibit free-radical polymerization, can diffuse through an aqueous medium and does not hydrolyze readily in such aqueous medium;
- said thin layer having a thickness of from a monomolecular layer to about 100 Angstroms;
- the amount of said activated-halogen monomer copolymerized in the thin layer ranging from about 0.01 milliequivalent to about 1.4 milliequivalent per gram of particles in the dispersion and not more than 3.0 milliequivalents for each gram of copolymer in the thin layer;
- the surfactant being used in a small, stabilizing amount up to about 0.25 milliequivalent per gram of structured particles.
A method for preparing a structured-particle latex comprising the steps of
- a. providing a temperature of from about 0.degree. C to about 80.degree. C, agitation and a free radical producing means in a preformed latex containing a small, stabilizing amount of a cationic surfactant or a mixture of a cationic surfactant and a nonionic surfactant but devoid of an anionic surfactant, the amount of the surfactant being less than the amount required to initiate new particles in the presence of additional monomer,
- b. providing in admixture with the preformed latex an ethylenically unsaturated, non-ionic monomer which is devoid of an activated-halogen and a nonionic, emulsion polymerizable, oil-soluble, ethylenically unsaturated, activated-halogen monomer which does not inhibit free-radical polymerization, can diffuse through an aqueous medium and does not readily hydrolyze in such aqueous medium;
- said activated-halogen monomer being provided in such a manner that the ratio of the activated-halogen monomer to total polymer is kept low at any given time, and
- c. maintaining the temperature and agitation until polymerization of the monomers is substantially complete;
- whereby there is formed a latex containing structured particles having activated-halogens chemically bound to the particle at or near the particle surface.
Dependencies are inferred from the claim text.