AssigneeAgence Nationale de Valorisation de la Recherche (ANVAR)
InventorsAlain Vidal, Gerard Riess, Jean-Baptiste Donnet
Estimating the term…
A process for grafting polymers on carbon black through a free radical mechanism comprising contacting of the black with the polymer and a thermal treatment. After formation of the carbon black mixture with at least one polymer, said mixture is degassed under vacuum at approximately room temperature, at least one substance acting as a solvent for said polymer is then introduced on said degassed mixture which is under vacuum, so as to form a solution of the latter containing the carbon black, said solution is heated with stirring at least at 50.degree. C until a carbon black bearing polymer grafts is obtained and the latter can, if desired, be separated by filtration or centrifugation of the unattached polymer solution. The carbon black products bearing polymer grafts as well as this carbon black itself are easily dispersed in solvents. They find valuable applications in paints, varnishes, printing inks, among others. The increase in dispersibility of the grafted carbon black improves its efficiency as a pigment, ultraviolet screening agent, filler, antioxidant, and the like.
A process for grafting polymers on carbon black through a transfer reaction free radical mechanism which comprises (1) forming a reaction mixture consisting of carbon black and at least one polymer containing a tertiary hydrogen atom, (2) degassing said mixture under vacuum at approximately room temperature, (3) adding at least one substance that is a solvent for said polymer to said degassed mixture, under vacuum, to form a solution of the said polymer containing the carbon black and (4) heating said solution to a temperature of at least 50.degree. C at which said reaction takes place and continuing the reaction until the desired carbon black bearing polymer graft is obtained.
A process for grafting polymers on carbon black through a transfer reaction free radical mechanism which comprises (1) forming a reaction mixture consisting of carbon black and at least one polymer from the group consisting of polystyrene, polyvinyl acetate, polypropylene, polymethyl methacrylate, acrylonitrile-styrene copolymers, polyvinyl chloride and propylene based copolymers, (2) degassing said mixture under vacuum at approximately room temperature, (3) adding at least one substance that is a solvent for said polymer to said degassed mixture, under vacuum, to form a solution of the said polymer containing the carbon black and (4) heating said solution to a temperture of a least 50.degree. C at which said reaction takes place and continuing the reaction until the desired carbon black bearing polymer graft is obtained.
Dependencies are inferred from the claim text.