Nickel and/or cobalt-coated steel with carburized interface
AssigneeRederiaktiebolaget Nordstjernan
InventorsLars H. Ramqvist, Nils Olle Grinder, Malte Sporrong, Per Enghag
Life of this patent
Estimating the term…
Abstract
A case-hardened, corrosion-resistant steel article is provided which comprises, applying a coating of nickel and/or cobalt to the surface of the article and then subjecting said coated article to carburization by heating said coated article to and maintaining it at an austenitic temperature under carburizing conditions for a time sufficient to effect carbon diffusion into the surface of the steel article. The corrosion resistance of the steel may be further enhanced by applying a thin layer of a final metal coat selected from the group consisting of Cr, Sn, Pb, Zn, Cu and Cd.
Claims5
A process for producing a corrosion resistant carburized steel article which comprises,
- applying a first metal coating comprising a layer of metallic nickel and/or cobalt of thickness ranging from about 5 to 20 microns to the surface of said steel article having a carbon content ranging up to about 0.5% by weight,
- carburizing said metal coated steel at an austenitizing temperature ranging from about 800.degree. to 1000.degree. C for a time sufficient to produce a carburized zone of thickness at least about 0.1 mm beneath said metal coating,
- rapidly cooling said article from its austenitizing temperature to produce a martensitic structure in at least said carburized zone,
- and then applying to said nickel and/or cobalt layer a second metal coating of over 2 microns thick of a metal selected from the group consisting of Cr, Sn, Pb, Zn, Cu and Cd,
- said nickel and/or cobalt layer having been cleaned of any deposited carbon formed thereon during the carburization step,
- whereby said article is characterized by an adherent first metal coating bonded to said steel and a second metal coating covering said first metal coating, said article being characterized further by improved resistance to corrosion and improved physical properties.
Dependencies are inferred from the claim text.