US 3,992,763 AGranted
Method of making powdered metal parts
AssigneeFederal-Mogul Corporation
InventorsRobert Nelson Haynie, Ramjee Pathak
Life of this patent
Estimating the term…
Abstract
Gas carburizing of a briquetted powder metal preform prior to hot forging of the preform to acquire a fully dense, carburized powdered metal part.
Claims6
A process for obtaining a substantially fully dense, carburized, low alloy ferrous, powdered metal part comprising the sequential steps of:
- a. briquetting a low alloy ferrous metal powder preform having a fixed uniform initial carbon content throughout both the case and inner core thereof, the briquetted preform having at least one surface thereof which in the final forged form is required to be of a certain case depth,
- b. sintering said preform at a temperature from 2000.degree.-2100.degree. F,
- c. carburizing said preform to substantially increase the initial carbon content thereof in said case by providing a controlled carbon atmosphere of rich endothermic gas and maintaining said preform in said controlled atmosphere for a predetermined period of time sufficient to obtain a desired case depth of final carbon content substantially greater than said initial carbon content of the case as well as the final carbon content of said inner core,
- d. forging said preform at a temperature range from about 1600.degree. to about 1750.degree. F to a density of 99.6% to 100% that of wrought density to obtain a forged part,
- e. cooling said forged part by quenching to thereby obtain a desired case depth.
2 more elements
A process for obtaining a substantially fully dense, carburized, low alloy ferrous, powdered metal part comprising the steps of:
- a. forming a briquetted preform, the briquetted preform having at least one surface thereof which in the final forged form is required to be of a certain case depth and wherein the upset ratio of said preform at said critical wear surface is greater than 10% and in the order of 40%.
- b. sintering said preform at a temperature from 2000.degree.-2100.degree. F
- c. simultaneously, during sintering, carburizing said preform by providing a controlled carbon atmosphere of endothermic gas and maintaining said preform in said controlled atmosphere for a predetermined period of time in the range of 20 to 40 minutes to obtain a desired case depth
- d. thereafter maintaining said preform in substantially the same atmosphere at a reduced temperature of from 1500.degree.-1750.degree. F for a further period of time in the range of 7 to 25 minutes to acquire a deeper, more controlled case depth
- e. forging said preform at a temperature ranging from 1600.degree.-1750.degree. F, including selecting the geometry of the said preform relative to the forging die cavity and orientating the preform within said die cavity so that the metal flows in the area of said one surface to thereby increase the case depth of the preform
- f. cooling said preform by quenching in an oil bath substantially immediately after forging but not until the temperature thereof has been allowed to substantially stabilize.
3 more elements
Dependencies are inferred from the claim text.