US 3,989,668 AGranted
Method of making a silicone elastomer and the elastomer prepared thereby
AssigneeDow Corning Corporation
InventorsChi-Long Lee, Gary M. Ronk
Life of this patent
Estimating the term…
Abstract
Mixing a hydroxyl endblocked polydiorganosiloxane, an organohydrogensiloxane, a platinum catalyst and a platinum catalyst inhibitor where the inhibitor is present in an amount of 0.0001 to 0.001 moles of inhibitor per 100 grams of hydroxyl endblocked polydiorganosiloxane and thereafter allowing the resulting mixture to cure, provides an elastomer.
Claims7
A method of making a silicone elastomer consisting essentially of
- mixing a hydroxyl endblocked polydiorganosiloxane having a viscosity of at least 1000 centipoise at 25.degree. C., an organohydrogensiloxane having at least 2.1 silicon-bonded hydrogen atoms per molecule, a platinum catalyst and a platinum catalyst inhibitor selected from the group consisting of acetylenic alcohols and a polyorganosiloxane consisting essentially of from 3 to 10 siloxane units in which (a) at least one siloxane unit is selected from the group consisting of RHSiO and
- R.sub.2 HSiO.sub.0.5
- and (b) at least one siloxane unit is selected from the group consisting of ##EQU1## and ##EQU2## where the sum of siloxane units in (a) and (b) is equal to at least three siloxane units, (c) any remaining siloxane units being selected from the group consisting of
- R.sub.3 SiO.sub.0.5, SiO.sub.2 and RSiO.sub.1.5
- where each siloxane unit of (c) does not exceed three siloxane units, where R is a monovalent radical selected from the group consisting of hydrocarbon radicals and perfluoroalkylethylene radicals, both having no more than six carbon atoms and R' is a monovalent hydrocarbon radical having a secondary or tertiary hydroxy substitution and having no more than ten carbon atoms, for each 100 parts by weight of hydroxyl endblocked polydiorganosiloxane there being present a sufficient amount of organohydrogensiloxane to provide a molar ratio of silicon-bonded hydrogen atoms per silicon-bonded hydroxyl radicals of from 1.5 to 4, the amount of platinum catalyst being present such that there is from 1 to 200 parts by weight platinum per 1 million parts by weight room temperature vulcanizable silicone elastomer, and the amount of platinum catalyst inhibitor being present in an amount such that there is present 0.0001 to 0.001 moles inhibitor per 100 grams of hydroxyl endblocked polydiorganosiloxene,
- allowing a composition obtained by the mixing procedure to set at room temperature until a cured silicone elastomer is obtained.
3 more elements
Dependencies are inferred from the claim text.