Insoluble electrode for electrolysis
AssigneeThe Dow Chemical Company
InventorsDonald Lee Caldwell, Raymond John Fuchs, Jr.
Life of this patent
Estimating the term…
Abstract
Electrodes are prepared by coating electrically conductive substrates with an electrically conductive film comprising a single-metal spinel of the formula Co.sub.3 O.sub.4. The coating can include modifier oxides selected from Groups III-B through VII-B, Groups III-A through V-A, and the Lanthanides and Actinides. Particularly suitable as modifier oxides are the oxides of zirconium, vanadium, titanium, lead, tantalum, tungsten, niobium, cerium, or molybdenum. These electrodes are particularly suitable for, but not limited to, use as the anode in an electrolytic chlorine cell wherein a diaphragm is interposed between an anode and a cathode in an aqueous electrolyte solution containing sodium chloride.
Claims16
An electrode for use in an electrolytic process, said electrode comprising an electroconductive substrate having coated thereon an effective amount of a single-metal spinel structure of Co.sub.3 O.sub.4.
An electrode for use in an electrolytic process, said electrode comprising:
- a substrate of titanium having a coating, on the surfaces which are to be in contact with the electrolyte, of a single-metal spinel structure of Co.sub.3 O.sub.4, said coating containing up to about 50 mole percent of a modifier oxide of zirconium oxide or vanadium oxide.
In an electrolytic cell comprising a housing, a cathode, an anode, and a diaphragm, said diaphragm being interposed between said cathode and anode, the improvement wherein the anode comprises a titanium substrate having a coating of Co.sub.3 O.sub.4 containing up to about 50 mole percent of zirconium oxide or vanadium oxide.
A process for preparing an electrode comprising an electroconductive substrate having an electroconductive coating thereon, which process comprises,
- coating an electroconductive substrate with a thermally decomposable metal-organic compound which, when thermally decomposed yields an adhered film of a single-metal spinel structure of Co.sub.3 O.sub.4 ,
- simultaneously coating the electroconductive substrate with a second thermally decomposable metal-organic, which, when thermally decomposed yields a modifier oxide of metal selected from Groups III-A, III-B, IV-A, IV-B, V-A, V-B, VI-B, VII-B, Lanthanides, or actinides of the Periodic Table of the Elements, said second metal-organic being present in an amount sufficient to provide up to about 50 mole percent of metal oxide, measured as metal, in the thermally decomposed coating;
- and subjecting said coated electroconductive substrate to a temperature in the range of about 200.degree. to about 600.degree.C for a period of time sufficient to oxidize the metal-organic compounds to their corresponding oxide forms, thereby obtaining an electrode comprising an electroconductive substrate having a coating thereon of Co.sub.3 O.sub.4 containing an evenly distributed modifier of metal oxide.