US 3,962,402 AGranted

Oxidation-leaching of chalcopyrite

AssigneeFreeport Minerals Corporation

InventorFreddie J. Touro

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method is described for the oxidation-leaching of chalcopyrite concentrates at high temperatures and pressures for the extraction of copper values as copper sulfate in which temperatures are maintained between about 425.degree. and 450.degree.F, oxygen partial pressures of between about 50 and 200 psi are provided, and levels of acidity are permitted to increase above about 50 grams of H.sub.2 SO.sub.4 per liter in order to obtain maximum rates of extraction of virtually all of the copper. Thereafter, while maintaining the temperature and pressure at elevated levels, the acidity of the slurry is reduced to between about 10 and 40 grams of H.sub.2 SO.sub.4 per liter in order to obtain reduction of dissolved iron to optimal levels. The resulting slurry is then cooled and further processed for the production of a very pure copper sulfate solution.

Claims4

Dependent claims

A process for the oxidation-leaching of chalcopyrite to produce a leach liquor containing at least about 87% of the copper in the chalcopyrite but less than 1.5 grams of iron per liter, comprising:

introducing an aqueous slurry of chalcopyrite ore concentrate into an autoclave;
treating, for approximately 5 to 15 minutes, the slurry in said autoclave at a temperature of about 425.degree. to 450.degree.F. and at an oxygen partial pressure of about 50 to 200 pounds per square inch while increasing the acid concentration of the slurry to a value in excess of about 50 grams of H.sub.2 SO.sub.4 per liter until at least about 87% of the copper in the concentrate is extracted as copper sulfate, the slurry having a dissolved iron concentration greater than about 1.5 grams per liter at the completion of the treatment;
and
then, reducing the acid concentration of the slurry to a final acid concentration of 10 to 40 grams of H.sub.2 SO.sub.4 per liter while it is still present in the autoclave and at a temperature of about 425.degree. to 450.degree.F. and an oxygen partial pressure of about 50 to 200 pounds per square inch, whereby iron is precipitated in the form of Fe.sub.2 O.sub.3.

1 more element

Dependencies are inferred from the claim text.