Catalyst for production of ethylene oxide
AssigneeShell Oil Company
InventorsRobert P. Nielsen, John H. La Rochelle
Life of this patent
Estimating the term…
Abstract
When supported silver materials are being prepared, deposits of from about 4.0 .times. 10.sup.-.sup.5 to about 8.0 .times. 10.sup.-.sup.3 gram equivalent weights per kilogram of finished product of ionic, higher alkali metals, i.e., ionic potassium, rubidium or cesium simultaneously with the deposit of silver improves the selectivity of these materials as catalysts for ethylene oxide production. Superior results are obtained with rubidium or cesium.
Claims29
A catalyst article comprising a porous refractory support having deposited on its exterior and pore surfaces from about 2% weight to about 20% by weight of silver and, coincidentally deposited with silver, a total of from about 4.0 .times. 10.sup..sup.-5 gew per kilogram of total catalyst to about 8.0 .times. 10.sup..sup.-3 gew per kilogram of total catalyst of alkali metal present in final form on the support in the form of an oxide in which the said oxide consists of an oxide of cesium or rubidium or mixtures thereof optionally combined with a minor proportion of the oxide of potassium relative to said rubidium and cesium.
A catalyst article consisting essentially of a porous alpha alumina support having a surface area of from about 0.03 m.sup.2 /g to about 2.0 m.sup.2 /g and having deposited on its exterior and pore surfaces from about 2% by weight to about 20% by weight of silver and, coincidentally deposited with the silver, a total of from about 2.0 .times. 10.sup..sup.-4 gew per kilogram of total catalyst to about 6.5 .times. 10.sup..sup.-3 gew per kilogram of total catalyst of alkali metal present in final form on the support in the form of an oxide in which the said oxide consists of an oxide of cesium or rubidium or mixtures thereof optionally combined with a minor proportion of the oxide of potassium relative to said rubidium and cesium.
A catalyst article comprising a porous support of siliceous composition having a surface area of from about 0.03 m.sup.2 /g to about 2.0 m.sup.2 /g and having deposited on its exterior and pore surfaces from about 2% by weight to about 20% by weight of silver and, coincidentally deposited with the silver, a total of from about 2.0 .times. 10.sup..sup.-4 gew per kilogram of total catalyst to about 6.5 .times. 10.sup..sup.-3 gew per kilogram of total catalyst of alkali metal present in final form on the support in the form of an oxide in which the said oxide consists of an oxide of cesium or rubidium or mixtures thereof optionally combined with a minor proportion of the oxide of potassium relative to said rubidium and cesium.
The process of preparing a supported silver catalyst which comprises impregnating a porous refractory catalyst support with a solution comprising solvent, silver salt sufficient to deposit on said support from 2% by weight to 20% by weight of silver and a salt of one or more higher alkali metals sufficient to deposit on said support a total of from about 4.0 .times. 10.sup..sup.-5 gew per kilogram of total catalyst to about 8.0 .times. 10.sup..sup.-3 gew per kilogram of total catalyst of at least one alkali metal in the form of a salt in which the said salt consists of a salt of cesium or rubidium or mixtures thereof optionally combined with a minor proportion of the salt of potassium relative to said rubidium and cesium;
- separating the impregnated support from excess impregnating solution and thereafter reducing the silver salt to silver metal at a temperature of from about 100.degree. to about 500.degree.C.
The process of preparing a supported silver catalyst which comprises
- a. impregnating a porous refractory catalyst support with a solution comprising solvent, silver salt sufficient to deposit from 2% by weight to 20% by weight of silver on said support and a salt of one or more higher alkali metals in which the said salt consists of a salt of cesium or rubidium or mixtures thereof optionally combined with a minor proportion of the salt of potassium relative to said rubidium and cesium, sufficient to deposit an amount of said alkali metal in excess of 8.0 .times. 10.sup..sup.-3 gew per kilogram of total catalyst on said support;
- b. separating the impregnated support;
- c. reducing the silver salt present on said impregnated support to silver metal at a temperature of from about 100.degree. to about 500.degree.C.
- d. contacting said impregnated support wherein silver is present as silver metal one or more times with an alkanol of 1 or 2 carbon atoms to selectively remove an amount of higher alkali metal present on said impregnated support such that the impregnated support so contacted contains 4.0 .times. 10.sup..sup.-5 to 8.0 .times. 10.sup..sup.-3 gew of higher alkali metal per kilogram of catalyst present in final form on the support in the form of an oxide in which the said oxide consists of an oxide of cesium or rubidium or mixtures thereof optionally combined with a minor proportion of the oxide of potassium relative to said rubidium and cesium;
- and
- e. separating the impregnated support from the alkanol contacting solution and drying to substantially remove the residual alkanol present in and on the impregnated support.
The process of preparing a supported silver catalyst which comprises
- a. simultaneously adding to a porous refractory catalyst support from about 3% by weight to about 15% by weight of silver in the form of a silver salt and from about 2.0 .times. 10.sup..sup.-4 gew per kilogram of total catalyst to about 6.5 .times. 10.sup..sup.-3 gew per kilogram of total catalyst of a higher alkali metal in the form of a water-soluble salt in which the said salt consists of a salt of cesium or rubidium or mixtures thereof optionally combined with a minor proportion of the salt of potassium relative to said rubidium and cesium, by contacting said support with an alkaline aqueous solution of said silver and higher alkali metal salts;
- and
- b. maintaining the product of step (a) at a temperature of from about 100.degree. to about 500.degree.C in the presence of a reducing agent, thereby converting the silver salt to silver metal.