Adhesive bonding of isotropic fiber webs to form pattern bonded composites

A tissue fiber laminate comprising outer plies of cellulosic tissue with the machine direction of said tissue plies the same, an intermediate substantially isotropic web of randomly oriented fibers, and lines of adhesive in a pattern between said outer plies of tissue attaching the tissue plies to each other with the fibers of the fiber web bonded in the adhesive lines,

• said outer tissue plies each having a finished basis weight of between about 10 and 20 g/yd..sup.2,
• said adhesive pattern comprising essentially continuous spaced lines extending transverse to the machine direction of said tissue plies, with the line width being more than about 0.010 inch and less than the spacing between lines, the spacing between lines being greater than about 0.060 inch, and covering between about 30-40 percent of the total area of the pattern, and the weight of the adhesive in the laminate being in the range of about 3 to about 20 g/yd..sup.2,
• said substantially isotropic web comprising textile fibers in the range of about 1/2 inch to about 3 inches in length and of 1/2 to 5 denier, and said web having a weight between about 5 and 10 g/yd..sup.2, the fibers being curled and crooked in the web as formed,
• and the fibers of said web being free of attachment to each other and to the tissue plies except where attached by the adhesive in the pattern to provide a fiber matrix which has a B/A factor less than about 1.5, said laminate having a grab tensile strength average of machine and cross direction of above about 6 lbs./in.

A process for the manufacture of tissue fiber laminates, comprising

• carrying a first cellulosic tissue web along a path parallel to its machine direction past an adhesive printing station,
• at said station printing on one surface of said first tissue web a pattern of adhesive in the form of essentially continuous, spaced lines extending transverse to the machine direction of said tissue web, and in an amount in the range of about 3 to about 20 g/yd..sup.2, said lines having a width greater than 0.010 inch and less than the spacing between lines, and the spacing between lines being not greater than about 0.060 inch, and controlling the penetration and lateral growth of the adhesive lines so that the adhesive lines remain clearly defined on the tissue web surface and cover between about 25 to 50 percent of the total area,
• laying a substantially isotropic textile fiber web of fibers of a length between about 1/2 inch to about 3 inches on the adhesive bearing surface of said first cellulosic tissue web such that the fibers of said fiber web become embedded in the adhesive lines,
• superposing a second tissue web and the first tissue web with the fiber web intermediate thereof and with the machine direction of said second tissue web aligned with the machine direction of said first tissue web, and
• hot calendering the first and second tissue webs and intermediate fiber web by passing said webs between calendar rolls heated to a temperature of 150.degree.-450.degree.F. and subjecting said webs to a nip pressure of 25-600 pli to force the adhesive on the first tissue web through the fiber web to the second tissue web to attach said tissue webs to each other while bonding the fibers of said fiber web in the pattern of said adhesive.

A method for the manufacture of tissue fiber laminates comprising

• introducing a substantially isotropic web of randomly distributed and well separated textile fibers of a length in the range between about 1/2 inch and about 3 inches, and of 1/2 to 5 denier between outer plies of cellulosic tissue wherein the machine direction of said tissue plies is the same, and
• attaching said tissue plies to each other while reinforcing said laminate to enhance the stretch to break and tensile strength in both the machine and cross directions of the laminate by bonding said isotropic web into a fiber matrix with a clearly defined pattern of essentially continuous spaced adhesive lines extending transverse to the machine direction of said tissue plies, with line width being more than about 0.010 inch and less than the spacing between lines, the spacing between lines being not greater than about 0.060 inch, and covering between about 25 and about 50 percent of the total area of pattern, and the weight of adhesive being in the range of about 3 to about 20 g/yd..sup.2, wherein the B/A factor for said adhesive pattern and said web is less than about 1.5, where A equals the straight line distance between bond points, and B equals the distance between bond points along the path of the crooked fiber segment, and such that the fiber segments contribute to the strength of the fiber matrix and provide a laminate having a grab tensile strength (average of machine and cross direction of above about 6 lbs./in.