Powa--method for coating and product
AssigneeFord Motor Company
InventorsMelville J. Camelon, Arend W. D. Vos
Life of this patent
Estimating the term…
Abstract
A method for painting automobiles and other articles of manufacture which admits of the use of medium to high concentration of metal pigments, can provide high gloss finish coatings and employs a low concentration of volatile solvents comprising application of a relatively thin, highly pigmented, water-based coating to a substrate, heat curing, application of an unpigmented or lightly pigmented powder coating that is transparent on curing, and heat curing of the powder coating. Products bearing unique finish coatings prepared by this method are claimed. This invention relates to the art of coating. More specifically, this invention relates to a novel method of coating substrates, particularly metal substrates, and to the products produced by such method.
Claims8
In a method for coating a substrate with diverse layers of coating material which comprises applying a heat-curable first coating material to said substrate, heating said substrate to at least partially cure said first coating material, applying a second coating material over said first coating material, and heating said substrate for a second time, the improvement wherein:
- I. said first coating material is applied to said substrate as a dispersion of solids in an aqueous solution of a water-soluble amine and consists essentially of about 6 to about 60 parts by weight particulate pigment and about 40 to about 94 parts by weight of thermosetting paint binder which consists essentially of
- A. 100 parts by weight acrylic paint binder resins consisting essentially of
- 1. about 5 to about 95 parts by weight of a solution polymer which is a carboxy-functional acrylic copolymer that
- a. is at least partially neutralized with said aqueous solution of water-soluble amine,
- b. is soluble in said aqueous solution,
- c. has average molecular weight (M.sub.n) in the range of about 3,000 to about 20,000 and
- d. has Tg in the range of -15.degree.C. to 50.degree.C. and,
- 2.
In a method for coating a substitute with diverse layers of coating material which comprises applying a heat-curable first coating material to said substrate, heating said substrate to at least partially cure said first coating material, applying a second coating material over said first coating material, and heating said substrate for a second time, the improvement wherein:
- I. said first coating material is applied to said substrate as a dispersion of solids in an aqueous solution of a water-soluble amine and consists of about 6 to about 60 parts by weight particulate pigment and about 40 to about 94 parts by weight of thermosetting paint binder which consists essentially of
- A. 100 parts by weight paint binder resins consisting essentially of
- 1. about 5 to about 50 parts by weight of a solution polymer which is a carboxy-functional copolymer of acrylic monomers that
- a. is at least parially neutralized with said aqueous solution of water-soluble amine,
- b. is soluble in said aqueous solution,
- c. has average molecular weight (M.sub.n) in the range of about 3,000 to about 20,000 and
- d. has Tg in the range of -15.degree.C. to 50.degree.C., and
- 2. about 50 to about 95 parts by weight of an emulsion polymer having functionality and hydroxy functionality and is a copolymer of acrylic monomers that
- a. is essentially insoluble in said aqueous solution,
- b. has average molecular weight (M.sub.n) in the range of about 3,000 to about 20,000, and
- c. has Tg in the range of -15.degree.C. to 50.degree.C., and
- B. about 15 to about 35 parts by weight of an amino resin crosslinking agent for said solution polymer and said emulsion polymer,
- Ii. said first coating material is applied to said substrate to an average thickness in the range of about 0.4 to about 1.2 mils,
- Iii. said first coating material is heated after application to said substrate and prior to application of second coating material to said substrate by maintaining said substrate at a temperature in the range of about 200.degree.F. to about 350.degree.F. for a time in the range of about 5 to about 15 minutes, and
- Iv. said second coating material is particulate film-forming material that converts to a continuous transparent coating upon maintaining said substrate at a temperature in the range of about 300.degree.F. to about 350.degree.F. for a time in the range of about 15 to about 30 minutes,
- V. said second coating material is applied to said substrate as particulate solids to an average thickness in the range of about 0.8 to about 1.7 mils, and
- Vi. said second coating material is heated by maintaining said substrate at a temperature in the range of 300.degree.F. to about 350.degree.F. for a time in the range of about 15 to about 30 minutes.
An article of manufacture comprising a substrate, a pigmented layer of a first coating material adhered to said substrate and a transparent layer of a second coating material opposite said substrate wherein:
- I. said first coating material is applied to said substrate as a dispersion of solids in an aqueous solution of a water-soluble amine and consists essentially of about 6 to about 60 parts by weight particulate pigment and about 40 to about 94 parts by weight of thermosetting paint binder which consists essentially of
- A. 100 parts by weight paint binder resins consisting essentially of
- 1. about 5 to about 95 parts by weight of a solution polymer which is a carboxy-functional acrylic copolymer that
- a. is at least partially neutralized with said aqueous solution of water-soluble amine,
- b. is soluble in said aqueous solution,
- c. has average molecular weight M.sub.n in the range of about 3,000 to about 20,000 and
- d. has Tg in the range of -15.degree.C. to 50.degree.C., and
- 2. about 5 to about 95 parts by weight of an emulsion polymer having functionality selected from carboxy functionality and hydroxy functionality and is an acrylic copolymer that
- a. is essentially insoluble in said aqueous solution,
- b. has average molecular weight (M.sub.n) in the range of about 3,000 to about 20,000, and
- c. has Tg in the range of -15.degree.C. to 50.degree.C., and
- B. about 15 to about 35 parts by weight of an amino resin crosslinking agent for said solution polymer and said emulsion polymer,
- Ii. said first coating material is applied to said substrate to an average thickness in the range of about 0.4 to about 1.2 mils,
- Iii. said first coating material is heated after application to said substrate and prior to application of said second coating material to said substrate by maintaining said substrate at a temperature in the range of about 200.degree.F. to about 350.degree.F. for a time in the range of about 5 to about 15 minutes, and
- Iv. said second coating material is a particulate thermosettable mixture consisting essentially of an epoxy-functional acrylic copolymer of monoethylenically unsaturated componds at least one of which is epoxy-functional and a cross-linking agent reactable with the epoxy functionality of said copolymer and selected from the group consisting of dicarboxylic acids and anhydrides of dicarboxylic acids, said crosslinking agent being present in an amount that provides about 0.3 to about 1.5 functional groups reactable with said epoxy-functional copolymer per functional group on said epoxy-functional copolymer and converts to a continuous, transparent coating upon maintaining said substrate to a temperature in the range of about 300.degree.F. to about 350.degree.F. for a time in the range of about 15 to about 30 minutes,
- V. said second coating material is applied to said substrate as particulate solids to an average thickness in the range of about 0.8 to about 1.7 mils, and
- Vi. said second coating material is heated by maintaining said substrate at a temperature in the range of 300.degree.F. to about 350.degree.F. for a time in the range of about 15 to about 30 minutes.
Dependencies are inferred from the claim text.