Process for producing fire resistant organic textile materials

Abstract

Organic fibrous materials especially cellulosic and other textiles are rendered flame resistant upon treatment with an emulsion containing either (1) an organic bromine containing material having at least 65% bromine such as polyvinylbromide, (2) polyvinylbromide and an N-methylol agent such as trimethylolmethylglycoluril, (3) polyvinylbromide and a metal oxide such as antimony oxide, and (4) polyvinylbromide, N-methylol agent and metal oxide. The emulsions are applied to various fibers by the pad-dry-cure technique. The finish contained the added quality of wrinkle resistance and rot resistance. The treated textiles, including polyester/cotton blends remain highly flame resistant through innumerable laundry cycles.