AssigneeThe Harshaw Chemical Company
InventorCaryl M. Sherman
Life of this patent
Estimating the term…
Abstract
A protective coating consisting of an aluminum or magnesium phosphate complex is used to encapsulate a wide variety of organic and inorganic particles. The coating is particularly applicable to organic and inorganic pigments and serves to improve the light, heat and chemical stability of these pigments. The coating is formed in situ by complexing the phosphate with the metal, preferably in the presence of ions of fluoride or fluoborate and depositing the same onto the surface of the particles.
Claims21
A process of forming a continuous, dense, protective, adherent skin of a metal phosphate complex on a solid particulate substrate wherein the metal is selected from the group consisting of aluminum and magnesium comprising
- a. blending a water soluble basic salt of the metal with an ortho phosphate or a precursor thereof, exclusive of a sodium salt, in an aqueous solution to form a complex thereof, the concentration of the blend being less than about 20 mg/ml of solution,
- b. maintaining the solution in a pH range of between about 1 and about 6 for a period of between a few seconds and about 20 minutes in the presence of the particulate substrate to slowly insolubilize the complex and to deposit it as a colloidal sol completely encapsulating the substrate,
- c. neutralizing the sol to terminate the formation of the complex, and
- d. recovering the encapsulated substrate.
A process of forming a continuous, dense protective and adherent coating of aluminum phosphate complex on a solid particulate substrate comprising:
- a. blending an aluminum compound selected from the group consisting of aluminum acetate and aluminum formate with an orthophosphate or with a phosphorous compound capable of forming an orthophosphate exclusive of sodium phosphate in an amount such that the mol ratio of aluminum to phosphorous in the coating is between 0.8 and 1.8;
- b. contacting the particulate substrate with a dilute solution containing between 0.5 and 20 mg. of the blend per ml of solution;
- c. maintaining the solution at a pH of between about 1 and about 6, at a temperature of less than about 40.degree.C for a period of between a few seconds and 20 minutes to form a colloidal sol of the complex having a particle size below about 600A.
- d. depositing the colloidal sol completely around the substrate to a thickness of between 25A and 300A,
- e. neutralizing the sol to terminate the formation of the complex, and
- f. recovering and drying the coated substrate at a temperature below the degradation temperature of the substrate.
A coated particle comprising a particulate substrate and a continuous, dense layer of protective coating completely encapsulating the substrate, said coating composed of a metal phosphate complex wherein the metal is selected from the group consisting of aluminum, magnesium and mixtures thereof;
- the coating comprising between about 5 and about 50% of the total particle weight and having a thickness of between about 25A and about 300A.
Dependencies are inferred from the claim text.