Smoke suppressants for halogen-containing plastic compositions
AssigneeN L Industries, Inc.
InventorsJoseph Schwarcz, Bernard Engelbart, Edward L. White
Life of this patent
Estimating the term…
Abstract
Zinc is added to a halogen-containing plastic composition with or without a flame retardant additive to serve as a smoke suppressant during combustion of the plastic.
Claims16
Method for forming a smoke suppressing combustible polyvinyl chloride composition comprising a polyvinyl chloride resin, a stabilizer, and zinc oxide comprising the steps of adding zinc oxide to the components of said polyvinyl chloride composition during formulation thereof, said zinc oxide added in amounts in the range of from about 0.2 to no more than about 1.0 part per 100 parts polymer resin.
Method for forming a smoke suppressing combustible polyvinyl chloride composition comprising adding finely divided zinc metal to the components of said polyvinyl chloride composition during formulation thereof said finely divided zinc metal added in amounts in the ranges of from about 0.2 to no more than about 1.0 part calculated as zinc oxide per 100 parts plymer resin.
Method for forming a smoke suppressing combustible polyvinyl chloride composition comprising a polyvinyl chloride resin, a stabilizer, a plasticizer, a flame retardant and zinc oxide comprising the steps of adding zinc oxide to the components of said polyvinyl chloride composition during formulation thereof said zinc oxide added in amounts in the range of from about 0.2 to no more than about 1.0 part per 100 parts polymer resin.
Method for forming a smoke suppressing combustible polyvinyl chloride composition comprising adding powdered zinc metal in combination with a flame retardant to the components of said polyvinyl chloride composition during formulation thereof said zinc metal added in amounts in the range of from about 0.2 to no more than about 1.0 part calculated as zinc oxide per 100 parts polymer resin.
A smoke suppressing combustible polyvinyl chloride composition comprising a vinyl chloride polymer, a stabilizer, and a smoke suppressant said smoke suppressant comprising zinc oxide in an amount in the range of from about 0.2 to no more than about 1.0 part per 100 parts polymer resin.
A smoke suppressing combustible polyvinyl chloride composition comprising a vinyl chloride polymer having a smoke suppressant incorporated therein said smoke suppressant comprising zinc dust added in amounts in the range from about 0.2 to no more than about 1.0 part, calculated as zinc oxide, per 100 parts polymer resin.
Method for forming a smoke suppressing combustible acrylonitrile-butadiene-styrene polymer containing an organic halide flame retardant comprising:
- adding zinc oxide to the components of said polymer during formulation thereof said zinc oxide added in amounts in the range of from about 0.2 to no more than about 1.0 part per 100 parts polymer resin.
Method for forming a smoke suppressing combustible polyester containing an organic halide flame retardant comprising:
- adding zinc oxide to the components of said polyester during formulation thereof said zinc oxide added in amounts in the range of from about 0.2 to no more than about 1.0 part per 100 parts resin.
Dependencies are inferred from the claim text.