Linear ultrahigh molecular weight polyethylene exhibiting a unique combination of rigidity and toughness and the process for the preparation thereof comprising inducing crystallization of the molten polyethylene at temperatures in the range of about 150.degree. to about 270.degree.C. by rapidly increasing the pressure applied from an initial level of about 1 to about 1000 atmospheres or more depending on temperature to a second level of about 2000-7000 atmospheres and higher and then cooling rapidly while maintaining a pressure sufficient to maintain the linear polyethylene in the solid phase until the temperature is below the crystalline melting point of linear polyethylene at atmospheric pressure. The resulting rigid, tough linear ultrahigh molecular weight polyethylene having a crystalline melting point of 142.degree. to 148.degree.C. at atmospheric pressure, as measured by differential thermal analysis, and by the absence of detectable low-angle X-ray scattering peaks indicative of crystalline spacings in the range of 50 A to 2000 A and by the presence of a predominance of fold spacings of about 10,000 A as determined by electron microscopy, and further characterized by exhibiting at room temperature an elastic modulus in the range of 165,000 to 500,000 psi., a density of 0.95 to 0.98 gram/cc at 25.degree.C. and a tensile impact strength in the range of 125-600 ft.lb/in.sup.2.
Linear polyethylene characterized by ultrahigh molecular weight, as determined from a melt index of essentially zero, indicating substantially no viscous flow above the crystalline melting point, an elastic modulus in the range of 340,000 to 500,000 psi., a tensile impact strength in the range of 140 to 600 ft.lb/in.sup.2, a crystalline melting point in the range of 142.degree.-148.degree.C. at atmospheric pressure, as measured by differential thermal analysis, a density of 0.95 to 0.98 grams/cc at 25.degree.C. and a unique crystalline from characterized by the absence of any detectable low-angle X-ray scattering peaks indicative of fold spacings in the range of 50-2000 A and by the presence, as seen in electron microscope photographs of cross sections, of a predominance of crystal spacings of about 10,000 A.
A rigid tough ultrahigh molecular weight linear polyethylene fabricated article characterized by being malleable and by exhibiting an elastic modulus in the range of 340,000 to 500,000 psi., a tensile impact strength in the range of 140 to 600 ft.lb/in.sup.2, a density of 0.95 to 0.98 g/cc at 25.degree.C., a crystalline melting point in the range of 142-148.degree.C., as measured by differential thermal analysis, and a unique crystalline form characterized by the absence of the low-angle X-ray scattering peaks indicating an absence of fold spacings of 50-2000 A normally observed in crystalline polyethylene, and by the presence, as seen in electron microscope photographs of cross sections of a predominance of crystal spacings of about 10,000 A.
Dependencies are inferred from the claim text.