Aromatic hydrocarbon isomer separation process
AssigneeUniversal Oil Products Company
InventorDonald H. Rosback
Life of this patent
Estimating the term…
Abstract
A process for the separation of the para-isomer from a hydrocarbon feed mixture comprising at least two bi-alkyl substituted monocyclic aromatic isomers, including the para-isomer, said isomers having from 8 to about 18 carbon atoms per molecule using a specially prepared adsorbent comprising a Y zeolite containing at the exchangeable cationic sites one or more selected cations. The feed mixture is passed through a bed of the adsorbent wherein the para-isomer is preferentially adsorbed within the adsorbent and thereafter recovered from the adsorbent. Novel feature of the process is the use of the specially prepared adsorbents which have faster adsorption-desorption rates for the desired para-isomer.
Claims19
A process for separating the para-isomer from a feed mixture comprising at least two bi-alkyl substituted monocyclic aromatic isomers, including the para-isomer, said isomers having from 8 to about 18 carbon atoms per molecule, which process comprises contacting said mixture with an adsorbent prepared by the steps of:
- a. contacting a base material comprising Y zeolite with an aqueous sodium hydroxide solution at first ion exchange conditions to effect the addition of sodium cations to said base material;
- b. treating the sodium-exchanged base material at second ion exchange conditions to effect the essentially complete exchange of sodium cations with one or more cations selected from the group consisting of potassium, cesium, and rubidium;
- and,
- c. drying the material at conditions to reduce the LOI at 900.degree. C. to less than about 10 weight percent thereby selectively adsorbing at adsorption conditions said para-isomer and thereafter recovering said para-isomer.
A process for separating the para-isomer from a feed mixture comprising at least two bi-alkyl substituted monocyclic aromatic isomers, including the para-isomer, said isomers having from 8 to about 18 carbon atoms per molecule, which process comprises the steps of:
- a. contacting at adsorption conditions said mixture with an adsorbent prepared by the steps hereinafter enumerated to effect the selective adsorption of para-isomer;
- b. withdrawing from the adsorbent a stream comprising less selectively adsorbed aromatic isomers;
- c. contacting the adsorbent with a desorbent material at desorption conditions to effect desorption of para-isomer from the adsorbent;
- and,
- d. withdrawing from the adsorbent a stream containing the para-isomer and desorbent material;
- wherein the adsorbent is prepared by the steps of:
- i. contacting a base material comprising a Y zeolite having a Na.sub.2 O/Al.sub.2 O.sub.3 ratio less than about 0.7 with an aqueous sodium hydroxide solution at first ion exchange conditions, including a temperature within the range of from about 50.degree. to about 250.degree. F. and a sodium hydroxide solution concentration of from about 0.5 to about 10 weight percent to increase the sodium cation content to a Na.sub.2 O/Al.sub.2 O.sub.3 ratio of greater than about 0.7;
- ii. treating the sodium-exchanged base material at second ion exchange conditions, including a pH sufficient to preclude the formation of the hydrogen form of the zeolite and a temperature within the range of from about 50.degree. to about 250.degree. F., to effect the essentially complete exchange of sodium cations with one or more cations selected from the group consisting of potassium, cesium, and rubidium;
- and,
- iii. drying the resulting material at conditions sufficient to reduce the LOI at 900.degree. C. to less than about 10 weight percent.
Dependencies are inferred from the claim text.