SiO.sub.2 -AlPO.sub.4 Glass batch compositions
AssigneeOwens-Illinois, Inc.
InventorNils Tryggve E. A. Baak
Life of this patent
Estimating the term…
Abstract
Glass batch compositions for producing low to medium expansion glasses having linear coefficients of thermal expansion in the range of from about 4.1 .times. 10.sup.-.sup.7 to about 19.0 .times. 10.sup.-.sup.7 in./in./.degree.C. over a temperature range from 0.degree.-300.degree..C. The glass batch compositions are capable of being melted at a temperature of about 1600.degree.C. and are composed essentially of a finely divided admixture of 70-87 mole percent SiO.sub.2 and 1.0-10 mole percent AlPO.sub.4 together with 0-21 mole percent of at least one RO.sub.2 oxide selected from the group consisting of from 0-14 mole percent TiO.sub.2 and 0-10 mole percent GeO.sub.2. The total mole percent of SiO.sub.2 and AlPO.sub.4 preferably constitute at least 79 mole percent of the total glass batch composition.
Claims13
A glass batch composition for producing a glass having a linear coefficient of thermal expansion of from about 4 .times. 10.sup.-.sup.7 to about 20 .times. 10.sup.-.sup.7 over the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of an admixture of the following components in the indicated ranges of mole percents of the total composition:
- Component Mole Percent Range ______________________________________ SiO.sub.2 70-87 AlPO.sub.4 5.0-10.0 TiO.sub.2 2.0-10.0. ______________________________________
A glass batch composition for producing a glass having a linear coefficient of thermal expansion within the range of from about 4 .times. 10.sup.-.sup.7 to about 20 .times. 10.sup.-.sup.7 over the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of an admixture of the following components in the indicated ranges of mole percents of the total batch composition:
- Component Mole Percent Range ______________________________________ SiO.sub.2 70-87 AlPO.sub.4 1.0-10 TiO.sub.2 4-14 GeO.sub.2 up to 10. ______________________________________
A glass batch composition for producing a glass having a low to medium linear coefficient of thermal expansion in the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of 75-85 mole percent SiO.sub.2, 4.9-10 mole percent AlPO.sub.4, 5-10 mole percent TiO.sub.2, together with at least one compatible glass batch component selected from the following group in an amount within the indicated range of mole percent amounts of the total glass batch composition:
- Component Mole Percent Range ______________________________________ P.sub.2 O.sub.5 0-5 B.sub.2 O.sub.3 0-5. ______________________________________
A glass batch composition for producing a glass having a linear coefficient of thermal expansion within the range of from about 4 .times. 10.sup.-.sup.7 to about 20 .times. 10.sup.-.sup.7 over the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of an admixture of the following components in the indicated ranges of mole percents of the total batch composition:
- Component Mole Percent Range ______________________________________ SiO.sub.2 75-80 AlPO.sub.4 1-10 TiO.sub.2 0-10 B.sub.2 O.sub.3 2.5-5 P.sub.2 O.sub.5 2.5-5. ______________________________________
A glass batch composition for producing a glass having a low to medium linear coefficient of thermal expansion in the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of the following components in the indicated ranges of mole percent amounts of the total glass batch composition:
- Component Mole Percent Range ______________________________________ SiO.sub.2 75-85 AlPO.sub.4 1-10 TiO.sub.2 2-10 B.sub.2 O.sub.3 4-5 GeO.sub.2 0-10. ______________________________________
A glass batch composition for producing a glass having a low to medium linear coefficient of thermal expansion in the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of 75-85 mole percent SiO.sub.2, 1-10 mole percent AlPO.sub.4, 2-10 mole percent TiO.sub.2, together with at least two glass batch components selected from the following group of components in an amount within the indicated mole percent range of the total glass batch composition:
- Component Mole Percent Range ______________________________________ GeO.sub.2 0-10 Al.sub.2 O.sub.3 0-5 B.sub.2 O.sub.3 0-4.5. ______________________________________
A glass batch composition for producing a glass having a low to medium linear coefficient of thermal expansion in the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of 75-85 mole percent SiO.sub.2, 1-10 mole percent AlPO.sub.4, 2-10 mole percent TiO.sub.2, together with at least two glass batch components selected from the following group of components in an amount within the inicated mole percent range of the total glass batch composition:
- Component Mole Percent Range ______________________________________ GeO.sub.2 0-10 Al.sub.2 O.sub.3 0-5 V.sub.2 O.sub.3 0-5. ______________________________________
A glass batch composition for producing a glass having a linear coefficient of thermal expansion within the range of from about 4 .times. 10.sup.-.sup.7 to about 20 .times. 10.sup.-.sup.7 over the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of an admixture of the following components in the indicated ranges of mole percents of the total batch composition:
- Component Mole Percent Range ______________________________________ SiO.sub.2 73-85 AlPO.sub.4 5-10 TiO.sub.2 6-10 CuO 3-10 B.sub.2 O.sub.3 0.-4.5 V.sub.2 O.sub.5 0-2.25. ______________________________________
A glass batch composition for producing a glass having a linear coefficient of thermal expansion within the range of from about 4 .times. 10.sup.-.sup.7 to about 20 .times. 10.sup.-.sup.7 over the temperature range of from 0.degree.-300.degree.C., said glass batch composition consisting essentially of an admixture of the following components in the indicated ranges of mole percents of the total composition:
- Component Mole Percent Range ______________________________________ SiO.sub.2 75-82 AlPO.sub.4 6.5-10. TiO.sub.2 5-6 CdO 1-10 B.sub.2 O.sub.3 0-4.5. ______________________________________
Dependencies are inferred from the claim text.