US 3,940,279 AGranted

Size-graded ternary batch for bonded basic refractory shapes

AssigneeCorning Glass Works

InventorsDonald L. Guile, Robert K. Smith

Life of this patent

Estimating the term…

Loading patent…

Abstract

A refractory of fused or dead-burned dolomitic grain bonded with fine magnesite. The dolomitic grain is divided into one coarse and one intermediate particle size fraction in the batch, while the magnesite is alone in the fine fraction. The fine, intermediate and coarse fractions are separated by large discrete gaps in the size distribution of particles resulting in a burned refractory of high hot strength and corrosion resistance to slags in basic oxygen furnaces. The width of each large gap in the particle size distribution is at least equivalent to the gap created by removing from a ground raw material batch, with a continuous particle size distribution, the particles retained on at least three consecutive primary Tyler sieves after screening (sizing) the batch.

Claims9

Dependent claims

A size-graded batch for the production of basic refractory bodies consisting essentially of, with percentages on the weight basis, a mixture of,

dead-burned magnesite and at least one refractory grain consisting essentially of on the oxide basis 50-67% MgO and 33-50% CaO and selected from the group of dead-burned grain and fused grain,
25-35% being a fine magnesite fraction whose particles are substantially all -100 Tyler mesh and composed of said dead-burned magnesite,
20-30% being an intermediate refractory grain fraction whose particles are substantially all in the range of -4+65 Tyler mesh, substantially all at least 2.sqroot.2 times the size of the largest allowed particle in said fine magnesite fraction, and composed of said refractory grain, and
40-50% being a coarse refractory grain fraction whose particles are substantially all in the range of -4+65 Tyler mesh, substantially all at least 2.sqroot.2 times the maximum allowed particle size in said intermediate refractory grain fraction and composed of said refractory grain.

1 more element

Dependencies are inferred from the claim text.