Method of producing composite bearing materials

A process for the continuous manufacture of carbon fibers reinforced shell bearings which process comprises:

• a. providing a continuous casting furnace and spaced therefrom, a cooling station;
• b. supplying continuously to said furnace a continuous trough of a backing material;
• c. supplying longitudinally of the internal base of said trough in said furnace continuous carbon fibers in the form of a tow, the fibers of said tow being supplied across the width of said trough;
• d. supplying in said trough in said furnace, molten bearing metal at a temperature at which it wets said carbon fibers, whereby said carbon fibers are incorporated in said molten bearing metal;
• e. passing said trough containing said molten bearing metal and incorporated carbon fibers from said furnace to said cooling station, during which passage the carbon fibers rise through said molten bearing metal to approach the surface of said molten bearing metal;
• and
• f. cooling and solidifying said molten bearing metal in said cooling station to form the shell bearing product in the form of a continuous strip of bearing metal containing incorporated therein continuous carbon fibers concentrated near the surface of said bearing.

A process for the continuous manufacture of carbon fiber reinforced shell bearings in which the bearing metal is a tin based alloy containing from 0.5 to 5.0 weight percent of titanium, vanadium or hafnium, which process comprises:

• a. providing a continuous casting furnace and a cooling station;
• b. supplying to said continuous casting furnace a continuous trough of backing material;
• c. supplying longitudinally in said continuous trough in said continuous casting furnace continuous carbon fibers in the form of a tow and said bearing metal in the molten form at a temperature at which said molten bearing metal wets the carbon fibers whereby the carbon fibers are incorporated into said molten bearing metal;
• and
• d. passing the trough containing molten bearing metal and said incorporated carbon fibers through the casting furnace to the cooling station and cooling and solidifying the bearing metal to form the shell bearing product in the form of a continuous strip.