Self-sealing vehicle tire and sealant composition
AssigneeGeneral Motors Corporation
InventorsPeter L. Stang, Joel V. Van Ornum
Life of this patent
Estimating the term…
Abstract
A vehicle tire is disclosed having an internal circumferential layer of self-sealing composition on an internal surface, particularly behind the tire tread. The sealant layer is initially made up of the combination of specific quantities of a high molecular weight curable butyl rubber, a low molecular weight curable butyl rubber, a liquid polybutylene tackifier, a partially hydrogenated block copolymer of styrene and a conjugated diene, carbon black and suitable curing agents for the butyl rubber components. When cured, this sealant layer effectively heals most punctures one-quarter inch in diameter or less in a vehicle tire at temperatures over the range of about - 20.degree. F. to 270.degree. F. without significant loss of air.
Claims4
A sealant composition for use in a vehicle tire to seal punctures therein up to about one-quarter inch in diameter formed in the operation of said tire, said composition consisting essentially of, by weight,
- 10 to 15 parts of a butyl rubber having an average molecular weight in the range of about 100,000 to 300,000,
- 6 to 10 parts of a butyl rubber having an average molecular weight in the range of about 10,000 to 30,000,
- 60 to 65 parts of a liquid polybutylene having an average molecular weight of about 500 to 5,000,
- 5 parts of a partially hydrogenated thermoplastic elastomeric block copolymer having the general molecular configuration A-(B-A).sub.1.sub.-5 wherein, prior to hydrogenation, each A is a monovinyl arene polymer block and each B is a conjugated diene polymer block, and only said diene block(s) are hydrogenated,
- 5 to 17 parts carbon black,
- and small but suitable amounts of crosslinking agents suitable for curing butyl rubbers.
A sealant composition for use in a vehicle tire to seal punctures therein up to about one-quarter inch in diameter formed in the operation of said tire, said composition consisting essentially of, by weight,
- 10 to 15 parts of a butyl rubber having an average molecular weight in the range of about 100,000 to 300,000,
- 6 to 10 parts of a butyl rubber having an average molecular weight in the range of about 10,000 to 30,000,
- 60 to 65 parts of a liquid polybutylene having an average molecular weight of about 500 to 5,000,
- 5 parts of a partially hydrogenated thermoplastic elastomeric block copolymer having the general molecular configuration A-(B-A).sub.1.sub.-5 wherein, prior to hydrogenation, each A is a styrene polymer block and each B is a conjugated diene polymer block of a diene taken from the group consisting of butadiene and isoprene, and only said diene block(s) are hydrogenated, said copolymer having a molecular weight in the range of about 70,000 to 150,000,
- 5 to 17 parts carbon black,
- and small but suitable amounts of crosslinking agents suitable for curing butyl rubbers.
A self-sealing rubber tire comprising a tread portion, a carcass portion and a self-sealing layer inside of said carcass portion, said self-sealing layer consisting essentially of, by weight, a cured composition formed from:
- 10 to 15 parts of a butyl rubber having an average molecular weight in the range of about 100,000 to 300,000,
- 6 to 10 parts of a butyl rubber having an average molecular weight in the range of about 10,000 to 30,000,
- 60 to 65 parts of a liquid polybutylene having an average molecular weight of about 500 to 5,000,
- 5 parts of a partially hydrogenated thermoplastic elastomeric block copolymer having the general molecular configuration A-(B-A).sub.1.sub.-5 wherein, prior to hydrogenation, each A is a monovinyl arene polymer block and each B is a conjugated diene polymer block, and only said diene block(s) are hydrogenated, and
- 5 to 17 parts carbon black.
A self-sealing rubber tire comprising a tread portion, a carcass portion and a self-sealing layer inside of said carcass portion, said self-sealing layer consisting essentially of, by weight, a cured composition formed from:
- 10 to 15 parts of a butyl rubber having an average molecular weight in the range of about 100,000 to 300,000,
- 6to 10 parts of a butyl rubber having an average molecular weight in the range of about 10,000 to 30,000,
- 60 to 65 parts of a liquid polybutylene having an average molecular weight of about 500 to 5,000,
- 5 parts of a partially hydrogenated thermoplastic elastomeric block copolymer having the general configuration A-(B-A).sub.1.sub.-5 wherein, prior to hydrogenation, each A is a styrene polymer block and each B is a conjugated diene polymer block of a diene taken from the group consisting of butadiene and isoprene, and only said diene block(s) are hydrogenated, said copolymer having a molecular weight in the range of about 70,000 to 150,000, and
- 5 to 17 parts carbon black.
Dependencies are inferred from the claim text.