Manufacturing of silicon-carbon composites materials
AssigneeGroup14 Technologies, Inc.
InventorsHenry R. COSTANTINO, Abirami DHANABALAN, Avery J. SAKSHAUG, Christopher TIMMONS, Rajankumar PATEL
Life of this patent
Estimating the term…
Abstract
Silicon-carbon composite materials and related processes are disclosed that overcome the challenges for providing amorphous nano-sized silicon entrained within porous carbon. Compared to other, inferior materials and processes described in the prior art, the materials and processes disclosed herein find superior utility in various applications, including energy storage devices such as lithium ion batteries.
Claims23
1-20. (canceled)
A process for preparing silicon-carbon composite particles comprising:
- providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
- heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
- providing silane gas corresponding to YCVI less than 0.5 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
- and
- wherein XSi of the process is greater than 50%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.
A process for preparing silicon-carbon composite particles comprising:
- providing a carbon scaffold comprising a pore volume, wherein the pore volume comprises greater than 70% microporosity;
- heating the porous carbon scaffold to a temperature between 350° C. and 550° C.;
- providing silane gas corresponding to YCVI less than 0.2 wherein YCVI=(mole of silane per hour)/(mol of carbon scaffold);
- and
- wherein XSi of the process is greater than 70%, wherein XSi=100×(mol of silicon in the silicon-carbon composite)/(mol silane feedstock), wherein the mol silicon in the silicon-carbon composite is determined from the silicon content in the silicon-carbon composite by thermogravimetric analysis.
Dependencies are inferred from the claim text.